Effect of friction stir processing on the corrosion behavior of an Mg-Zn-Ca composite containing 1.0 wt% MgO
Jian Han,Xinya Chen,Zhen Liu,Shuang Zhang,Minfang Chen,Zhiyong Mao,Zhen Luo,Xi Zhang,Yinbao Tian,Yangchuan Cai
DOI: https://doi.org/10.1016/j.matchar.2022.112249
IF: 4.537
2022-10-01
Materials Characterization
Abstract:In this study, an innovative Mg-based composite composed of Mg-Zn-Ca containing 1.0 wt% MgO nanoparticles was processed by friction stir processing (FSP) to induce shear plastic deformation. This treatment was aimed at optimizing the basic microstructure of the traditional Mg-Zn-Ca composite with added MgO nanoparticles to improve the material performance for application as a biomedical material. After FSP, the grains were noticeably refined from 1.78 ± 0.25 μm to 1.04 ± 0.17 μm, and a basal texture appeared, which led to a reduction in the in vitro degradation rate of 30%. Furthermore, the high grain boundary density and local misorientation at the grain boundaries accelerated the formation of the passivation film, and the evenly distributed MgO nanoparticles led to the formation of a uniform passivation film. In conclusion, FSP treatment of Mg composites can improve the corrosion resistance based on the Mg-Zn-Ca composite with added nanoparticles if suitable processing parameters are selected. In this study, FSP was used to optimize the biomedical composite, which improved the corrosion and mechanical properties, and provided a certain method and theoretical basis for optimizing the field of biomedical materials.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing