Abstract:Hypersonic vehicles encounter hostile service environments of thermal/mechanical/chemical coupling, so thermal protection materials are crucial and essential. Ceramizable composites have recently attracted intensive interest due to their ability to provide large-area thermal protection for hypersonic vehicles. In this work, a novel ceramizable composite of quartz fiber/benzoxazine resin modified with fused SiO2 and h-BN was fabricated using a prepreg compression molding technique. The effects of the fused SiO2 and h-BN contents on the thermal, mechanical, and ablative properties of the ceramizable composite were systematically investigated. The ceramizable composite with an optimized amount of fused SiO2 and h-BN exhibited superb thermal stability, with a peak degradation temperature and residue yield at 1400 °C of 533.2 °C and 71.5%, respectively. Moreover, the modified ceramizable composite exhibited excellent load-bearing capacity with a flexural strength of 402.2 MPa and superior ablation resistance with a linear ablation rate of 0.0147 mm/s at a heat flux of 4.2 MW/m2, which was significantly better than the pristine quartz fiber/benzoxazine resin composite. In addition, possible ablation mechanisms were revealed based on the microstructure analysis, phase transformation, chemical bonding states, and the degree of graphitization of the ceramized products. The readily oxidized pyrolytic carbon (PyC) and the SiO2 with a relatively low melting point were converted in situ into refractory carbide. Thus, a robust thermal protective barrier with SiC as the skeleton and borosilicate glass as the matrix protected the composite from severe thermochemical erosion and thermomechanical denudation.

A novel Ti 3 SiC 2 -CaB 6 modified Al-coated carbon fiber/boron phenolic resin ceramizable composite (ACF/BPRC) with excellent long-term oxidative corrosion resistance and high temperature load-bearing capacity

High temperature flexural strength, microstructure, phase evolution and anti-oxidation mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composite modified with TiB2 and B4C

Oxidation resistance, ablation resistance and in situ ceramization mechanism of Al-coated carbon fiber/boron phenolic resin ceramizable composites modified with Ti3SiC2

Oxidation Behavior of Carbon Fibers in Ceramizable Phenolic Resin Matrix Composites at Elevated Temperatures

Oxidation and Ablation Behavior of a Ceramizable Resin Matrix Composite Based on Carbon Fiber/phenolic Resin

A Novel Fused SiO2 and h-BN Modified Quartz Fiber/Benzoxazine Resin Ceramizable Composite with Excellent Flexural Strength and Ablation Resistance

Oxidation Behavior of Carbon/Carbon Composites Coated with A Si-Siox/Bn-B2o3-Sio2-Al2o3 Oxidation Protection System at Intermediate Temperature

Enhanced Mechanical Property, High-Temperature Oxidation and Ablation Resistance of Carbon Fiber/phenolic Composites Reinforced by Attapulgite

Oxidation Behavior Of A 2d-Sicf/Bn/Sibcn Composite At 1350-1650 Degrees C In Air

Long‐term oxidation and ablation behavior of Cf/ZrB2–SiC composites at 1500, 2000, and 2200°C

Long-term oxidation and ablation behavior of C<sub>f</sub>/ZrB<sub>2</sub>-SiC composites at 1500, 2000, and 2200C

Mechanical property, oxidation resistance, and ceramization mechanism of MoSi2-SiB6 reinforced phenolic resin matrix composites

Thermal behavior of phenolic-based ceramizable composites modified by nano-aluminum oxide

Microstructural Regulation, Oxidation Resistance and Mechanical Properties of Cf/SiC/SiHfBOC Composites Prepared by Chemical Vapor Infiltration with Precursor Infiltration Pyrolysis

A Low-Temperature Prepared Composite Coating to Protect SiC-coated C/C Composites Against Oxidation in a Wide Temperature Range for Long-Life Service

Thermal oxidation and compressive failure behavior of ZrSi2–B4C modified phenolic resin-based composite

Oxidation Resistance of In Situ Reaction/Hot Pressing Synthesized Ti2AlC–20% TiB2 Composite at 600–900 °C in Air

Lightweight and Multiscale ZrO2-SiOC Coated Carbon/phenolic Composites with Enhanced Oxidation and Ablation Resistance

Oxidation Resistance of Carborane-Containing Polymer Coatings for Carbon–carbon Composites at Low and Medium Temperatures

The Oxidation of SiC Fiber and SiC Fiber Reinforced Boron Phenolic Resin Composite

Oxidation and ablation behaviors of carbon fiber/phenolic resin composites modified with borosilicate glass and polycarbosilane interface