Variations in perpendicular magnetic and electrical transport properties of ferrimagnetic (0 0 1) NiCo 2 O 4 films

Jiseok Park,Joonghoe Dho

DOI: https://doi.org/10.2139/ssrn.4638989

IF: 3.097

2024-01-16

Journal of Magnetism and Magnetic Materials

Abstract:We fabricated epitaxial NiCo 2 O 4 films on (0 0 1) MgAl 2 O 4 substrates by varying the pulsed-laser energy density from 1.31 to 2.46 J/cm 2 , while keeping all other parameters fixed. X-ray diffraction measurements revealed that the increase in energy density increased the film deposition rate from 0.022 to 0.078 nm/s, while resulting in the decrease of the full-width at half-maximum of the rocking curve and out-of-plane lattice constant. At room temperature, the films grown at an intermediate energy density range of 1.97–2.13 J/cm 2 exhibited more distinctive perpendicular magnetic anisotropy and magnetic domain structure compared to those grown at high or low energy densities. On the other hand, the lower the laser energy density, the more pronounced the perpendicular magnetic anisotropy becomes at low temperatures. In addition, the ferrimagnetic-to-paramagnetic transition temperature of the film increased with the energy density, reaching a maximum of approximately 390 K at energy densities above 2.13 J/cm 2 . Furthermore, temperature-dependent resistivity indicated that the metallic behavior in the films grown above 2.13 J/cm 2 was retained up to ∼ 500 K, which is much higher than the ferrimagnetic transition temperature. These results suggest that pulsed-laser energy density can serve as an alternative parameter for controlling the perpendicular magnetic properties and enhancing the metallic behavior of the (0 0 1) NiCo 2 O 4 film.

materials science, multidisciplinary,physics, condensed matter