Abstract:The magnetic anisotropy and magnetic interactions at the interface between Fe and NiO(001) were investigated. Depending on the growth conditions of the NiO(001) layers and the post-annealing temperature, the preferential magnetization direction of the ultrathin Fe layer grown on a NiO(001) layer changed from in-plane to a direction perpendicular to the film plane. The lattice constant of the NiO(001) layers parallel to the growth direction increased with O$_2$ flow rate, while that parallel to the in-plane were locked onto the MgO(001) substrate regardless of the growth conditions of the NiO layers. Moreover, perpendicular magnetization was observed only when the NiO layer was grown with O$_2$ flow rates higher than 2.0 sccm corresponding to oxygen-rich NiO. X-ray magnetic circular dichroism measurements revealed an enhancement in anisotropic orbital magnetic moments similar to the origin of perpendicular magnetic anisotropy at the Fe/MgO(001) interface. The interfacial magnetic anisotropy energies were 0.93 and 1.02 mJ/m$^2$ at room temperature and at 100 K, respectively, indicating less temperature dependence. In contrast, the coercivity $H_c$ exhibited a significant temperature dependence. Although no signature of exchange bias or unidirectional loop shift was observed, $H_c$ was strongly dependent on the NiO layer thickness, indicating that the exchange interaction at the interface between the ferromagnetic and antiferromagnetic layers was not negligible, despite the NiO(001) being a spin-compensated surface.

Anisotropic Ferromagnetic Behaviors in Highly Orientated Epitaxial NiO-based Thin Films

Interfacial Orbital Preferential Occupation Induced Controllable Uniaxial Magnetic Anisotropy Observed in Ni/NiO(110) Heterostructures

Ferromagnetism in Antiferromagnetic NiO-based Thin Films

Manipulated Magnetic Coercivity and Spin Reorientation Transition in NiCo2O4 Films

Annealing Temperature Dependent Ferromagnetic Behaviors Observed in Highly Orientated Pure NiO Thin Films

Perspective on Epitaxial NiCo2O4 Film as an Emergent Spintronic Material: Magnetism and Transport Properties

Mechanism of Doping-Induced Orientation of Magnetic Phase in a Sol–Gel-Derived Ni0.5Zn0.5Fe2O4/BaTiO3 Multiferroic Thin Film with High Magnetoelectric Coupling

Perpendicular magnetic anisotropy of an ultrathin Fe layer grown on NiO(001)

Spin reorientation transition in (110)-oriented NiCo2O4 epitaxial thin films

Perpendicular Magnetic Anisotropic NiCo2O4 Epitaxial Films with Tunable Coercivity

Thickness Dependence of Room Temperature Ferromagnetism Observed in Fe-doped NiO Thin Films

Perpendicular Magnetic Anisotropic Epitaxial Films with Tunable Coercivity

Ferroelectric Strain Modulation of Antiferromagnetic Moments in Ni/Nio Ferromagnet/Antiferromagnet Heterostructures

Antiferromagnetic Proximity Effect in Epitaxial CoO/NiO/MgO(001) Systems.

Ferromagnetic Behaviors in NiO-based Nanofibers Synthesized by Electrospinning Method

Nonvolatile manipulation of electronic and ferromagnetic properties of NiO–Ni epitaxial film by ferroelectric polarization charge

Thickness-modulated Anisotropic Ferromagnetism in Fe-doped Epitaxial HfO2 Thin Films

In-plane Spin Reorientation Transition in Fe/NiO Bilayers on Ag(1,1,10)

Anomalous Hall Effect and Perpendicular Magnetic Anisotropy in Ultrathin Ferrimagnetic NiCo$_2$O$_4$ Films

Electronic states and structural characterization in single-crystal Fe–Ni–O alloy thin films grown by molecular beam epitaxy

Transfer of magnetic anisotropy in epitaxial Co/NiO/Fe trilayers