Enhancing Interfacial Ferromagnetism and Magnetic Anisotropy of CaRuO3/SrTiO3 Superlattices via Substrate Orientation
Wenxiao Shi,Jie Zheng,Zhe Li,Mengqin Wang,Zhaozhao Zhu,Jine Zhang,Hui Zhang,Yunzhong Chen,Fengxia Hu,Baogen Shen,Yuansha Chen,Jirong Sun
DOI: https://doi.org/10.1002/smll.202308172
IF: 13.3
2023-12-02
Small
Abstract:A robust ferromagnetic phase with strong in‐plane magnetic anisotropy is revealed at the (111)‐oriented heterointerface between paramagnetic CaRuO3 and diamagnetic SrTiO3. The Curie temperature as high as ≈155 K and the saturation magnetization as large as ≈1.3 μB per formula unit are obviously superior to those of the (001)‐oriented counterparts and are comparable to the typical itinerant ferromagnet SrRuO3. Artificial oxide heterostructures have provided promising platforms for the exploration of emergent quantum phases with extraordinary properties. One of the most interesting phenomena is the interfacial magnetism formed between two non‐magnetic compounds. Here, a robust ferromagnetic phase emerged at the (111)‐oriented heterointerface between paramagnetic CaRuO3 and diamagnetic SrTiO3 is reported. The Curie temperature is as high as ≈155 K and the saturation magnetization is as large as ≈1.3 μB per formula unit for the (111)‐CaRuO3/SrTiO3 superlattices, which are obviously superior to those of the (001)‐oriented counterparts and are comparable to the typical itinerant ferromagnet SrRuO3. A strong in‐plane magnetic anisotropy with six‐fold symmetry is further revealed by the anisotropic magnetoresistance measurements, presenting a large in‐plane anisotropic field of 3.0–3.6 T. More importantly, the magnetic easy axis of the (111)‐oriented superlattices can be effectively tuned from 〈112 ̄ 1〉 to 〈11 ̄0 〉 directions by increasing the layer thickness of SrTiO3. The findings demonstrate a feasible approach to enhance the interface coupling effect by varying the stacking orientation of oxide heterostructures. The tunable magnetic anisotropy also shows potential applications in low‐power‐consumption or exchange spring devices.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology