Abstract:The diminutive additions of nickel (Ni) element have been fused to Sn-1.5Ag-0.5 mass% Cu (SAC155) lead-free solder alloy. The study was examined experimentally and computationally (using JMatPro software program) the microstructural features, thermal behavior, density, thermal diffusivity, and conductivity as well as tensile stress strain of the Sn-1.5Ag-0.5Cu-x mass %Ni (x = 0.00, 0.05, 0.10, 0.20, and 0.50) solder alloys (SAC155-xNi). The fusing additions of Ni have a little impact on the melting point of SAC155 alloy which increasing from 502 to . The microstructure of SAC155 solder alloy included coarse grains of β-Sn besides, large eutectic regions, and embedded IMCs of Ag 3 Sn and Cu 6 Sn 5 . The computed values of Gibbs free energy (G) during solidification of the β-Sn phase, Ag 3 Sn, and Sn 3 Sn 4 IMCs show the stability at , , and , respectively. The SAC155-xNi alloys involved finer β-Sn grains, large fibrous eutectic regions, (Cu,Ni) 6 Sn 5 and (Cu,Ni) 3 Sn 4 IMCs. The G of Cu 6 Sn 5 decreased from to when Ni content increased up to 0.25 mass %, then stable and steady at with more addition of Ni element. The formation of the (Cu, Ni) 6 Sn 5 and (Ni, Cu) 3 Sn 4 IMCs is motivated by the lowest Gibbs free energy, especially when Ni mass% is added to a sufficient level. The measured and computed values of specific heat at constant pressure ( C p ) of SAC155-xNi alloys show a good matching especially at lower temperatures and a little mismatch at high temperatures which decreases with increasing Ni content. The activation energy of atomic arrangement (Q) increased from 11.36 to with increasing Ni content in SAC155-xNi alloys. Thermal diffusivity (α) and conductivity (κ) of SAC155-xNi gradually decreased with increasing temperature in the range from 303 to 423 K and/or Ni content in alloys. The measured values of (κ) are slightly lower than the computed value at similar temperatures of the SAC155-xNi alloys. The decrease in (κ) may be assigned to scattering the electrons or reducing the phonon contributions due to the presence of various solute atoms and different IMCs. The results of stress-strain graphs reveal the enhancement of YS and UTS for all Ni-containing alloys. The improvement of the yield stress (YS) and ultimate tensile strength (UTS) of Ni-containing alloys is attributed to the uniform distribution of the IMCs, the reduction of β-Sn grain size, and the smoothed enlargement of the eutectic region.

Dispersion and incorporation of TiO 2 and SiC nano-particles in SAC alloy: SIMS and DFT study

Nanocomposite SAC solders: morphology, electrical and mechanical properties of Sn–3.8Ag–0.7Cu solders by adding Co nanoparticles

Wettability and Shear Strength of SAC305 Based Composite Solder with Co-Doping X (ni or Al2O3) and CNTs Reinforcements

Effects of ZrO2 Nano-Particles' Incorporation into SnAgCu Solder Alloys: An Experimental and Theoretical Study

Microstructural, compositional and hardness evolutions of 96.5Sn–3Ag–0.5Cu/TiC composite solder under thermo-migration stressing

In-situ fusion process and Cu–Sn compounds evolution mechanism of nano-intermetallic compound mixed solder joints

Performance and interfacial reaction mechanism of nano-IMC-mixed solder paste with variable melting point

Accelerated solid-liquid interdiffusion bonding of Cu joint using a Cu10Ni alloy mesh reinforced SAC305 composite solder

Improved shear property of Sn-3.0Ag-0.5Cu/Ni micro solder joints under thermal shock between 77 K and 423 K by adding TiO2 nanoparticles

Synthesis and analysis of the structure of modified-Al2O3 particles used to increase the strength and electrical conductivity of lead-free solder based on Sn–Ag–Cu

Study on the dual inhibition behavior of interfacial IMCs in Cu/SAC105/Cu joint by adopting SiC nanowires and nanocrystalline Cu substrate

Effect of Nano-Cu 6 Sn 5 upon development mechanism of Cu–Ni–Sn compounds and mechanical characteristics for mixed solder joints

Microstructural Examination and Thermodynamic Analysis of Sn-1.5Ag-0.5Cu-x mass% Ni Lead-Free Solder Alloys

Review on the Al2O3 nanoparticle reinforcement effect on thermal and mechanical properties of SAC alloys

Effects of TiC nanoparticle addition on microstructures and mechanical properties of Sn-58Bi solder joints

Effect of the addition of CeO 2 nanoparticles on the microstructure and shear properties of Sn-57Bi-1Ag solder alloy

Real-time monitoring of soldering process in SAC composite solder paste: movement and interaction of dopant particles in solder paste

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Effect of the addition of Cu6Sn5 nanoparticles on the growth of intermetallic compounds at the interfaces of Sn3.0Ag0.5Cu solder joints

Preparation and Properties of Nano-sized SiC Particles Reinforced ADC12 Aluminum Matrix Composites

Effect of Au-deposited ceramic nanoparticles on SAC305/Cu solder joints