Abstract:The diminutive additions of nickel (Ni) element have been fused to Sn-1.5Ag-0.5 mass% Cu (SAC155) lead-free solder alloy. The study was examined experimentally and computationally (using JMatPro software program) the microstructural features, thermal behavior, density, thermal diffusivity, and conductivity as well as tensile stress strain of the Sn-1.5Ag-0.5Cu-x mass %Ni (x = 0.00, 0.05, 0.10, 0.20, and 0.50) solder alloys (SAC155-xNi). The fusing additions of Ni have a little impact on the melting point of SAC155 alloy which increasing from 502 to . The microstructure of SAC155 solder alloy included coarse grains of β-Sn besides, large eutectic regions, and embedded IMCs of Ag 3 Sn and Cu 6 Sn 5 . The computed values of Gibbs free energy (G) during solidification of the β-Sn phase, Ag 3 Sn, and Sn 3 Sn 4 IMCs show the stability at , , and , respectively. The SAC155-xNi alloys involved finer β-Sn grains, large fibrous eutectic regions, (Cu,Ni) 6 Sn 5 and (Cu,Ni) 3 Sn 4 IMCs. The G of Cu 6 Sn 5 decreased from to when Ni content increased up to 0.25 mass %, then stable and steady at with more addition of Ni element. The formation of the (Cu, Ni) 6 Sn 5 and (Ni, Cu) 3 Sn 4 IMCs is motivated by the lowest Gibbs free energy, especially when Ni mass% is added to a sufficient level. The measured and computed values of specific heat at constant pressure ( C p ) of SAC155-xNi alloys show a good matching especially at lower temperatures and a little mismatch at high temperatures which decreases with increasing Ni content. The activation energy of atomic arrangement (Q) increased from 11.36 to with increasing Ni content in SAC155-xNi alloys. Thermal diffusivity (α) and conductivity (κ) of SAC155-xNi gradually decreased with increasing temperature in the range from 303 to 423 K and/or Ni content in alloys. The measured values of (κ) are slightly lower than the computed value at similar temperatures of the SAC155-xNi alloys. The decrease in (κ) may be assigned to scattering the electrons or reducing the phonon contributions due to the presence of various solute atoms and different IMCs. The results of stress-strain graphs reveal the enhancement of YS and UTS for all Ni-containing alloys. The improvement of the yield stress (YS) and ultimate tensile strength (UTS) of Ni-containing alloys is attributed to the uniform distribution of the IMCs, the reduction of β-Sn grain size, and the smoothed enlargement of the eutectic region.

Review on the Al2O3 nanoparticle reinforcement effect on thermal and mechanical properties of SAC alloys

A review on nanodispersed lead-free solders in electronics: synthesis, microstructure and intermetallic growth characteristics

Synthesis and analysis of the structure of modified-Al2O3 particles used to increase the strength and electrical conductivity of lead-free solder based on Sn–Ag–Cu

Investigation of Microstructure and Mechanical Properties of SAC105 Solders with Sb, In, Ni, and Bi Additions

Nanoparticle-reinforced solder alloys: A comprehensive review of recent formulation properties, and mechanical performance

Effects of ZrO2 Nano-Particles' Incorporation into SnAgCu Solder Alloys: An Experimental and Theoretical Study

Microstructural Examination and Thermodynamic Analysis of Sn-1.5Ag-0.5Cu-x mass% Ni Lead-Free Solder Alloys

Dispersion and incorporation of TiO 2 and SiC nano-particles in SAC alloy: SIMS and DFT study

Microstructure, elastic modulus and shear strength of alumina (Al2O3) nanoparticles-doped tin–silver–copper (Sn–Ag–Cu) solders on copper (Cu) and gold/nickel (Au/Ni)-plated Cu substrates

Microstructural, mechanical, and wear properties of Sn-based solder alloy modified with graphite nanoparticles

Effect of Au-deposited ceramic nanoparticles on SAC305/Cu solder joints

Numerical evaluation of the mechanical response of Sn-Ag-Cu lead-free solders of various silver contents

Microstructural investigations and mechanical properties of pure lead-free (Sn–3.0Ag–0.5Cu and Sn–4.0Ag–0.5Cu) solder alloy

Atomistic analysis of the thermomechanical properties of Sn–Ag–Cu solder materials at the nanoscale with the MEAM potential

Uniaxial and cyclic stress-strain behavior of lead-free solders at nanoscale

Soldering of Passive Components Using Sn Nanoparticle Reinforced Solder Paste: Influence on Microstructure and Joint Strength

Effect of the addition of CeO 2 nanoparticles on the microstructure and shear properties of Sn-57Bi-1Ag solder alloy

The influences of reactive nanoparticles alloying on grain boundary and melting properties about Sn3.0Ag0.5Cu solder

The role of Ni minor additions on the mechanical characteristics of Sn-1.5Ag-0.5 wt.% Cu (SAC155) Pb-free solder alloy

Effect of Nano-Al2o3 Reinforcement on the Microstructure and Reliability of Sn–3.0Ag–0.5Cu Solder Joints

The influences of Ag nanoparticles on voids growth and solderability about Sn3.0Ag0.5Cu/Cu solder joint