Abstract:An increase in hydrostatic stress improves the plasticity of metallic materials. However, for some special components, such as large thin-walled components with high ribs, excessive hydrostatic stress can cause several problems that make it impossible to prepare such components using plastic forming methods. In this study, the effect of hydrostatic stress on the deformation behavior of large thin-walled components with high ribs was investigated using a combination of numerical simulations and theoretical derivations. The results indicated that excessive hydrostatic stress leads to die failure, causing metal flow difficulties, uneven deformation, inconsistent mechanical properties, and reduced forming accuracy. Therefore, a low-hydrostatic-stress extrusion method was proposed by adjusting the contact friction, metal flow direction and displacement, and force boundary conditions to reduce the hydrostatic compressive stress. These principles are mainly reflected in the following three aspects: First, the size of the difficult deformation zone was reduced by changing the friction conditions from dry friction to fluid friction or boundary friction to reduce the frictional resistance. Second, the high-stress zone was eliminated by changing the metal flow direction, adjusting the strain state from unidirectional to multi-directional flow, shortening the metal flow path, and reducing the metal flow resistance. Third, the strong compressive stress state in the three directions was weakened by regulating the force boundary conditions and changing the loading method from one-way extrusion to multi-directional loading. Based on these principles, a series of new forming technologies have been developed, such as actively counteracting frictional resistance, slotting, and ditching on dies for long-lasting lubrication, multi-directional short-range metal flow, drawing-assisted extrusion, and multi-directional active loading. The adoption of these technologies realizes the labor-efficient formation of large thin-walled components with high ribs and provides the formed members with high precision and uniform mechanical properties.

Flow defects of rib-web components in isothermal local-loading forming process

A non-sequential isothermal local-loading forming process for large-scale rib-web components

Numerical and experimental investigation on precision forming of ribbed tube by cold drawing process

Effect of cold process drawing parameters on the formability and microstructure of ribbed cladding tubes

Multi-pass rolling-extrusion of large-scale thin-walled square tube with longitudinal inner ribs

Deformation mechanism of ZK61 magnesium alloy cylindrical parts with longitudinal inner ribs during hot backward flow forming

Influence of Process Parameters on Thinning Ratio and Fittability of Bellows Hydroforming

Loading conditions constrained wrinkling behaviors of thin-walled sheet/tube parts during metal forming

Study on generating rolling method for manufacturing cylindrical parts with external cross ribs

Height inhomogeneity in flow forming of thin-walled tubes with helical grid-stiffened ribs: characterization, mechanism and control method

Deformation Patterns in Hydroforming of Thin-Walled Y-Shaped Tube

Enhancing the Robustness of Rib-Groove Filling and Strain Homogeneity in the Isothermal Forging of Titanium Alloy Multi-Rib Components

Investigation on low hydrostatic stress extrusion technology for forming of large thin-walled components with high ribs

Springback and longitudinal bow in chain-die forming U and hat channels

Experimental and simulation study for rewelding defects during the flow process of Semi-solid die casting

Web crippling investigation of perforated aluminium lipped channels under interior-one-flange loading condition

An analytical model for designing defect-free sheet metal profiles with height-variable cross sections manufactured by Flexible Roller Beading

Numerical simulation of material flow and defect formation during FSW to predict weld failure location

Metal flowing of involute spline cold roll-beating forming

Machining-induced residual stress and deformation during Mg–Li alloy thin-walled rib-web parts milling

Analysis and suppression of flange wrinkling in AHSS chain-die forming channels with a curved axis