Reversible phase transformation and doubly-charged anions at the surface of simple cubic RbC60

Roberto Macovez,Andrea Goldoni,Luca Petaccia,Ingrid Marenne,Paul A. Bruehwiler,Petra Rudolf

DOI: https://doi.org/10.1103/PhysRevLett.101.236403

2008-10-27

Abstract:The simple cubic phase of a RbC60 thin film has been studied using photoelectron spectroscopy. The simple cubic-to-dimer transition is found to be reversible at the film surface. A sharp Fermi edge is observed and a lower limit of 0.5 eV is found for the surface Hubbard U, pointing to a strongly-correlated metallic character of thin-film simple cubic RbC60. A molecular charge state is identified in the valence band and core level photoemission spectra which arises from C602- anions and contributes to the spectral intensity at the Fermi level.

Materials Science,Strongly Correlated Electrons

What problem does this paper attempt to address?

This paper mainly studied the reversible phase transition of the simple cubic phase of RbC\(_{60}\) thin films and the doubly - charged anions present on their surfaces. Specifically, the author explored the reversibility of the transformation of RbC\(_{60}\) thin films from the simple cubic phase to the dimer phase and the change in the molecular charge state during this process by using Photoelectron Spectroscopy (PES) technology.

### Main problems
1. **Reversible phase transition**: One of the key problems that the paper attempted to solve was whether the transformation from the simple cubic phase to the dimer phase on the surface of RbC\(_{60}\) thin films was reversible. In bulk materials, this transformation is usually irreversible, but on the thin - film surface, the author found that this transformation was reversible.
2. **Existence of doubly - charged anions**: Another important problem was to identify and explain the existence of the doubly - charged anions (C\(_{60}^{2-}\)) observed in the simple cubic phase and their contribution to the surface metallic properties. These anions provided significant spectral intensity near the Fermi level, indicating that they play an important role in the surface metallic properties.

### Research methods
- **Experimental techniques**: Photoelectron Spectroscopy (PES) technology was used, especially the experiments carried out on the SuperESCA beamline, to measure the valence - band and core - level spectra of RbC\(_{60}\) thin films with high resolution.
- **Sample preparation**: RbC\(_{60}\) thin films were grown on Ag(100) single crystals by the standard distillation method to obtain C\(_{60}\)-terminated face - centered cubic (fcc) RbC\(_{60}\)(111) thin films.
- **Temperature control**: The simple cubic phase and the dimer phase were obtained by rapidly cooling the fcc phase to different temperatures, and the reversibility of the phase transition was tested by temperature cycling.

### Main findings
- **Reversible phase transition**: The transformation from the simple cubic phase to the dimer phase on the surface of RbC\(_{60}\) thin films was reversible, which was in contrast to the irreversible transformation in bulk materials.
- **Doubly - charged anions**: The existence of C\(_{60}^{2-}\) anions was observed in the simple cubic phase. These anions provided significant spectral intensity near the Fermi level, indicating that they play an important role in the surface metallic properties.
- **Surface Hubbard U**: By analyzing the photoelectron spectroscopy data, the lower limit of the surface Hubbard U was determined to be 0.5 eV, indicating that the surface of RbC\(_{60}\) thin films has strongly correlated metallic properties.

### Conclusion
Through detailed photoelectron spectroscopy research, the paper revealed the reversible phase transition from the simple cubic phase to the dimer phase on the surface of RbC\(_{60}\) thin films and the important role of doubly - charged anions in the surface metallic properties. These findings are helpful for in - depth understanding of the electronic structure and phase - transition behavior of fullerene compounds and provide important experimental basis for further research in related fields.