Green sucrose-sol-gel combustion synthesis of a CuO-based oxygen carrier for NO x emission reduction and its cyclic reaction performance

Xianxing Huang,Min Zheng,Hua Wang,Kang Li,Jun Wu

DOI: https://doi.org/10.1016/j.fuproc.2023.107924

IF: 8.129

2023-07-31

Fuel Processing Technology

Abstract:Chemical-looping combustion has attracted considerable attention as a novel combustion technology. In this study, precursors were prepared using the sol–gel method with sucrose complexation followed by combustion to synthesize CuO-based oxygen carriers (OCs) supported on an Al 2 O 3 –TiO 2 template. The sucrose complexing agent inhibited the release of NO x during combustion. When the molar ratio of sucrose to Cu(NO 3 ) 2 ·3H 2 O (R) was <0.36, the NO x produced included both NO and NO 2 . When R exceeded 0.73, the NO x produced by precursor combustion was primarily NO, and its concentration was greatly reduced. A slower heating rate also reduced the release of NO x . At a heating rate of 1 °C/min, the release of NO x was 80% lower than that at a heating rate of 10 °C/min. All OCs were stable for ten redox cycles. Increasing the sucrose complexant content resulted in an initial increase in the reactivity of the OCs followed by a decrease. The best performing OC had an R value of 0.36 and yielded the highest mean CO 2 percentage (61.27%). When R exceeded 1.00, the sintering and agglomeration of CuO-based OCs were severe, and the mean CO 2 yield was reduced to 57.20%. The carbon deposits from the CH 4 decomposition were completely oxidized to CO 2 by the air in the reactor.

energy & fuels,engineering, chemical,chemistry, applied