Abstract:Graphite-like carbon nitride (g-C3N4) and borate modified layered double hydroxides (LDH-B) were successfully fabricated by thermal pyrolysis and modified aqueous miscible organic solvent treatment methods, respectively. Then these nano-additives were introduced to prepare polypropylene-grafted maleic anhydride (PP-g-MA)/g-C3N4 and PP-g-MA/LDH-B nanocomposites using a modified solvent mixing strategy. Several important parameters of the nanocomposites including thermal, mechanical and UV-blocking properties were investigated. Results indicated that pure g-C3N4 exhibited 347.6 and 427.2 degrees C increase in onset decomposition temperature under air and nitrogen conditions, respectively, compared with LDH-B. In case of PP-g-MA nanocomposites, both T-10 and T-50 (the temperature at 10% and 50% weight loss, respectively) were improved by 14.6 and 27.7 degrees C, respectively, by the addition of g-C3N4 while those only increased by 2.3 and 17.8 degrees C upon introducing LDH-B. Furthermore, PP-g-MA/g-C3N4 system showed a remarkable increment (9.8 degrees C) in crystallization temperature while an increase of 4.2 degrees C for PP-g-MA/LDH-B nanocomposite. Introducing g-C3N4 and LDH-B into PP-g-MA led to a reduction of 28% and 19% in pHRR, respectively. It was noted that the incorporation of g-C3N4 caused significant improvement in storage modulus from 2445.0 MPa for neat PP-g-MA to 2783.5 MPa for PP-gMA/g-C3N4 while that of PP-g-MA/LDH-B was dramatically decreased by 27.3%. Optical results indicated that PP-g-MA/g-C3N4 was rendered fascinating UV adsorption ability relative to PP-g-MA/LDH-B. It is expected that the novel two-dimensional nanomaterial could bring new creativity into polymer composites. (C) 2015 Elsevier Ltd. All rights reserved.

Synthesis of polypropylene functionalized with a trace amount of reactive functional groups and its utilization in graft-type nanocomposites

Fabrication of High-Performance PP/Graphene Nanocomposites Via Friedel–Crafts

Preparation of Isotactic Polypropylene-Grafted Multiwalled Carbon Nanotubes (Ipp-G-mwnts) by Macroradical Addition in Solution and the Properties of Ipp-G-Mwnts/Ipp Composites

A Convenient, Highly-Efficient Method for Preparation of Hydroxyl-Terminated Isotactic Poly（propylene） and Functional Di-Block Copolymer

Controllable Synthesis of a Well-defined Polypropylene grafted Silica Nanoparticles and Its Effect on Crystallization Behavior of Polypropylene

Synthesis of multifunctional polypropylene via solid phase cografting and its grafting mechanism

Preparation of Polypropylene and Polystyrene with NCO and NH2 Functional Groups and Their Applications in Polypropylene/polystyrene Blends

Isothermal crystallization of polypropylene/surface modified silica nanocomposites

Synthesis of Multifunctional Polypropylene Via Solid Co-Grafting and the Mechanism Study.

Modification of mechanical and color properties of polypropylene with colored nano‐SiO<sub>2</sub> prepared from diatomite

Modification Of Mechanical And Color Properties Of Polypropylene With Colored Nano-Sio2 Prepared From Diatomite

Effect of hydrophobic nano‐silica/β‐nucleating agents on the crystallization behavior and mechanical properties of polypropylene random copolymers

A Novel Method for Functionalization of Polypropylene with Oligomer of Glycidyl Methacrylate: Characterization of Copolymers

In Situ Compatibilization of Polypropylene and Polystyrene-Grafted Nano-Sized TiO2 in the Presence of Friedel–Crafts Catalyst

Mechanical properties and structural characteristics of PP/PP-g-SBR nanocomposites prepared by dynamical photografting

Polypropylene Nanocomposites Attained by In Situ Polymerization Using SBA-15 Particles as Support for Metallocene Catalysts: Effect of Molecular Weight and Tacticity on Crystalline Details, Phase Transitions and Rheological Behavior

Progress in synthesis methods of polypropylene-based block copolymers

Polypropylene/silica Nanocomposites in Situ Prepared Via Sol-Gel Reactions Using Porous Spherical Poly(propylene- G -(Styrene- Alt -Maleic Anhydride)) Granules As Reaction Loci

Graphite-like Carbon Nitride and Functionalized Layered Double Hydroxide Filled Polypropylene-Grafted Maleic Anhydride Nanocomposites: Comparison in Flame Retardancy, and Thermal, Mechanical and UV-shielding Properties

Polypropylene nanocomposites produced by in‐situ grafting of maleic anhydride using different mixing procedures

The Structure and Physical Properties of Polypropylene and Thermoplastic Olefin Nanocomposites Containing Nanosilica