Brazing SMART tungsten alloys to RAFM steels by Titanium-Zirconium-Beryllium brazing alloy

Veronika Kirillova,Nikita Popov,Julia Gurova,Diana Bachurina,Xiaoyue Tan,Aleksei Suchkov

DOI: https://doi.org/10.2139/ssrn.4665620

IF: 1.905

2024-03-08

Fusion Engineering and Design

Abstract:Various DEMO designs imply the use of tungsten as plasma facing material and RAFM steels as structural material. LOCA concerns have shifted the focus from pure tungsten to tungsten smart alloys (SA), thus presenting a new challenge of obtaining joints of SA with RAFM steels. In this work, high-temperature brazing via TiZr4Be amorphous alloy is suggested as a prospective production technology. Use of Ta as a compensating interlayer between SA and RAFM is suggested. WCrY/Ta/Eurofer and WCrZr/Ta/CLAM joints are characterised by the formation of brittle Ta 2 Be structures (700 HV 0,1 ) that are found mainly in the Ta/RAFM seam. According to the results of mechanical shear strength tests, the fracture occurs primarily in the SA/Ta seam. Joints with Ta successfully withstand 100 cycles of thermal cycling tests in the 300–600 °C temperature range without failure. The average shear strength after thermal cycling tests drops from 187±96 MPa and 104±42 MPa to 47±11 MPa and 56±21 MPa for WCrY/Ta/Eurofer and WCrZr/Ta/CLAM joints, respectively.

nuclear science & technology