Abstract:The effect of rolling temperature on the incomplete recrystallization behavior and the relationship to mechanical properties in 0.06C–4Mn-1.2Cr (wt.%) steel was investigated. Three plates of experimental steel were produced by hot rolling at different temperatures and intercritical annealing processes in this study. The microstructure of experimental steels was examined by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), electron backscatter diffraction (EBSD), and transmission electron microscope (TEM). The mechanical properties of test steel were examined by impact test and tensile test. Austenite reversion and cementite precipitation-dissolution was numerically simulated under the assumption of local equilibrium. With the decrease of hot rolling temperature from 1000 °C to 800 °C, the uniform equiaxed prior austenite grains microstructures changed to heterogeneous microstructures of laminated and ultrafine prior austenite grains arranged alternatively. The tensile and impact tests revealed that the medium manganese steels rolling at 800 °C had an excellent combination of mechanical properties. Elongation had a great relationship with retained austenite fraction and stability. The fractography of impact specimens was examined to explore the toughening mechanism of the micro-laminated steels. The steel with uniform equiaxed grain structure exhibited a relatively low tensile strength of 750 MPa and low elongation of ∼20% and an extremely poor low-temperature toughness of ∼40 J at −40 °C. An enhanced low-temperature toughness (∼233 J at −40 °C), as well as an improved tensile strength (823 MPa) and higher elongation of ∼40%, was obtained in the steel with heterogeneous microstructures. The content of austenite in heterogeneous microstructure is twice that in uniform equiaxed grain structure. And cementite dissolved more thoroughly in the heterogeneous microstructure. The high austenite content of heterogeneous microstructures enabled the steel to be significantly stronger and ductile, which contributed to the high tensile strength and elongation to some extent. It is concluded that the effect of interface decohesion resulted in the occurrence of delamination. And the high austenite content and delamination greatly improved the low-temperature toughness of experimental steel.

Analysis of medium manganese steel through cold-rolling and intercritical annealing or warm-rolling

Microstructure and Mechanical Properties of Medium Mn Steel Containing 3%al Processed by Warm Rolling

Intercritically Annealed Medium-Manganese Steel: Insights into Microstructural and Microtextural Evolution, Strain Distribution, and Grain Boundary Characteristics

Effect of rolling temperature on microstructure and mechanical properties of medium manganese steel

Microstructure evolution and tensile behaviour of a cold rolled 8 wt\% Mn medium manganese steel

Optimizing Microstructure and Mechanical Properties of Cold-Rolled Medium-Mn Steel Through Intercritical Annealing and Warm Rolling

Current opinion in medium manganese steel

Ultra-Fine Heterogeneous Microstructure Enables High Strength-Ductility in a Cold-Rolled Medium Mn Steel

Microstructure and Mechanical Properties of a Novel Cold Rolled Medium-Mn Steel with Superior Strength and Ductility

Tailoring retained austenite and mechanical property improvement in Al–Si–V containing medium Mn steel via direct intercritical rolling

Stepwise Warm Rolling for Synergistic Strength and Ductility Enhancement in Heterolamellar Medium-Mn Steel

Warm Stamping Technology of the Medium Manganese Steel

Microstructure and Mechanical Properties of Hot-Rolled Medium-Mn Steel Containing 3% Aluminum

Super-High-Strength and Formable Medium Mn Steel Manufactured by Warm Rolling Process

Microstructural characteristics and tensile behavior of medium manganese steels with different manganese additions

Microstructure Evolution and Mechanical Properties of Medium Carbon Martensitic Steel during Warm Rolling and Annealing Process

Microstructural evolution and strain hardening behavior of a novel two-stage warm rolled ultra-high strength medium Mn steel with heterogeneous structures

Microstructure evolution and mechanical properties of metastable austenitic medium Mn steel fabricated by warm caliber rolling

Intercritical annealing to achieve a positive strain-rate sensitivity of mechanical properties and suppression of macroscopic plastic instabilities in multi-phase medium-Mn steels

Effect of Cooling Practice on the Mechanical Properties of Medium‐Manganese Aluminum‐Alloyed Steels after Intercritical Annealing Quench and Partition Treatment

Effect of annealing time on microstructure and mechanical properties of Fe–C–Mn–Al–Si steel