Superior hydrogen embrittlement resistance of CoCrNi-based medium-entropy alloy via coherent precipitation and grain boundary strengthening

Saiyu Liu,Zhao Xu,Yujie Zhu,Rongjian Shi,Kewei Gao,Xiaolu Pang

DOI: https://doi.org/10.1016/j.corsci.2024.112483

IF: 7.72

2024-09-26

Corrosion Science

Abstract:The strength and HE resistance of CoCrNi-based medium-entropy alloys were simultaneously improved via adding 264 at.ppm boron and the precipitation of nanoscale coherent L1 2 (γ'-type) particles. After aging treatment, the proportion of intergranular cracking decreased from 58.2 % in the solution-treated alloy to 27.6 %. Meanwhile, the yield strength increased by 102 %, and the ductility decreased by only 35.9 %. Notably, the elongation loss is only 9.4 %. On one hand, the added boron segregates to the grain boundaries (GBs), enhance the GB cohesive strength. On the other hand, precipitated L1 2 captures H, thereby reducing the concentration of diffusible H in the matrix and decelerating the diffusion rate of H. During plastic deformation, the L1 2 particles impedes the movement of dislocations and reduces stress concentration at GBs. This is associated with the presence of a completely coherent interface between the precipitated phase and face centered cubic matrix. This research provides insights into the beneficial effects of L1 2 phase precipitation and GB boron segregation on the HE resistance of M/HEAs.

materials science, multidisciplinary,metallurgy & metallurgical engineering