Excellent mechanical properties of CoNiCr-based MP159 multicomponent alloys at ambient and cryogenic temperatures

Dian Wang,Biao Pei,Zhong Wang,Xiaofeng Niu,Zhongnan Bi,Junwei Qiao,Bin Gan

DOI: https://doi.org/10.1016/j.intermet.2023.107836

IF: 4.075

2023-01-23

Intermetallics

Abstract:The L1 2 -strengthened high-entropy alloys (HEAs) exhibit excellent mechanical properties. The commercial CoNiCr-based MP159 superalloy with high configuration entropy up to that of HEAs is revisited. And the coherent L1 2 nano precipitates with different sizes and volume fractions are introduced into MP159 alloys by tuning the aging time. Especially at 298Â K, the alloys after aging for 10Â h can achieve a good combination of 1360Â MPa high tensile strength and 41% tensile strain. In contrast, the tensile strength is as high as 1710Â MPa, and the tensile strain remains at 45% at cryogenic temperatures, much better than most of HEAs with similar composition. Importantly, the optimal size of the precipitates is calculated to be 41Â nm. The present work provides a basic guidance for developing nano-precipitated CoNiCr-based alloys with high mechanical performances.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering