Abstract:In this study, the rice husk (RH) of "Joha rice" a unique rice variety of Assam (Northeast India) has been used as raw materials for synthesis of ash and silica powder. The combustion of the husk at 500°C for 1 h followed by further treatment at 800°C for 2 h in muffle furnace produces white rice husk ash (RHA). One part of RHA was kept as untreated, and the another part was acid treated. Silica was extracted from the untreated ash in the form of sodium silicate by treating with 2.5M NaOH at the boiling temperature. Then, silica was precipitated from sodium silicate by slow addition of 2.5M H 2 SO 4 . The broad x‐ray diffraction (XRD) pattern and characteristic peaks at d‐spacing, 8.3792 and 4.1489 with specific 2θ at ∼21.3° reveal the presence of amorphous SiO 2 as major phase in the ash (both acid treated and untreated). The characteristic Fourier transform infrared (FTIR) spectroscopic peaks at 470–450, 801, and 1100 cm −1 for different modes of Si‐O‐Si vibrations also support the presence of silica. The scanning electron micrographs (SEMs) revealed the morphology of the RHA as fine particles undergoing agglomeration probably due to hydrogen bonding between surface silanol groups present. The irregular rough morphology is a characteristic of the amorphous nature of the samples. The energy‐dispersive X‐ray analysis (EDX) showed that RHA composition was dominated by elements Si and O for both untreated and acid‐treated samples. For acid‐treated sample, the amount of Si and O is found to be comparatively higher than the untreated one due to surface cleaning. The point of zero charge (pH PZC ) of the prepared samples was determined by a simple pH metric method. The pH PZC of the untreated RHA was found to be ∼ 9.8 ± 0.2. However, almost similar pH PZC values of the acid‐treated RHA silica and commercial silica (∼6.6 ± 0.2) indicate the effectiveness of acid treatment prior processing.

Synthesis of White Silica From "Joha Rice Husk" (A Special Rice Variety of Assam, India), Characterization and Determination of Its Point of Zero Charge (pH PZC )

Beneficial Utilization of Rice Husk Ash (rha) As A New Sorbent for Removal of Antimony (iii) from Water

Preparation of highly dispersed nanosilica from rice husk by aprecipitation method combined with high pressure homogenization

Synthesis of silica and carbon-based nanomaterials from rice husk ash by ambient fiery and furnace sweltering using a chemical method

The preparation of silica white from fly ash and its characterization

Production and characterization of silica materials from rice husk ash by different combustion processes

Reduction in time required for synthesis of high specific surface area silica from pyrolyzed rice husk by precipitation at low pH.

THE ACID-BASE PROPERTIES OF AMORPHOUS SILICA FROM STRAW AND RICE HUSK

Silica White Obtained from Rice Husk in a Fluidized Bed

Synthesis of Rice Husk Nanosilica using the Hydrothermal Method

Influence of pre-treatment processes on the purity and characteristics of silica extracted from rice husk

Chemical and structural properties of silica obtained from rice husk and its potential as a catalytic support

Mechano-chemical conversion of rice husk ash and gasifier-derived rice husk ash into porous silicon

Extraction of Silica from Rice Husk 71

Silica precipitation from rice husk ash leachate: optimization and kinetic analysis

Comparative Study Of Water-Leaching And Acid-Leaching Pretreatment On The Thermal Stability And Reactivity Of Biomass Silica For Viability As A Pozzolanic Additive In Cement

review of rice husk silica as a heterogeneous catalyst support

Processing and Characterization of Nano Silica and Iron Oxide Coated Silica Composites Extracted from Rice Hulls

Preparation of Silica by Alkaline-Heating and Precipitation Method from Corn Straw Ash

A Detailed Study of the Effects of Pyrolysis Temperature and Feedstock Particle Size on the Preparation of Nanosilica from Rice Husk

SYNTHESIS OF NANO-SILICA FROM LOA KULU RICE HUSK USING THE SOL-GEL METHOD