Abstract:Two MgB2 samples were prepared using the spark plasma sintering (SPS) technique at different temperatures—950 °C (S1) and 975 °C (S2)—for 2 h under 50 MPa pressure to study the influence of preparation temperature on different facets, namely those perpendicular (PeF) and parallel (PaF) to the compression direction of uniaxial pressure during the SPS of MgB2 samples. We analyzed the superconducting properties of the PeF and PaF of two MgB2 samples prepared at different temperatures from the curves of the critical temperature (TC), the curves of critical current density (JC), the microstructures of MgB2 samples, and the crystal size from SEM. The values of the onset of the critical transition temperature, Tc,onset, were around 37.5 K and the transition widths were about 1 K, which indicates that the two samples exhibit good crystallinity and homogeneity. The PeF of the SPSed samples exhibited slightly higher JC compared with that of the PaF of the SPSed samples over the whole magnetic field. The values of the pinning force related to parameters h0 and Kn of the PeF were lower than those of the PaF, except for Kn of the PeF of S1, which means that the PeF has a stronger GBP than the PaF. In low field, the most outstanding performance was S1-PeF, whose critical current density (JC) was 503 kA/cm2 self-field at 10 K, and its crystal size was the smallest (0.24 μm) among all the tested samples, which is consistent with the theory that a smaller crystal size can improve the JC of MgB2. However, in high field, S2-PeF had the highest JC value, which is related to the pinning mechanism and can be explained by grain boundary pinning (GBP). With an increase in preparation temperature, S2 showed a slightly stronger anisotropy of properties. In addition, with an increase in temperature, point pinning becomes stronger to form effective pinning centers, leading to a higher JC.

Effect of sintering temperature under high pressure in the uperconductivity for MgB2

The Influence of Preparation Temperature on the Different Facets of Bulk MgB2 Superconductors

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

High-Pressure Synthesis of Mgb2 Superconductor with T-C above 39 K

Superconducting Properties of MgB 2 Prepared by High Pressure and Ambient Pressure

Effect of Heat Treatments under High Isostatic Pressure on the Transport Critical Current Density at 4.2 K and 20 K in Doped and Undoped MgB2 Wires

Effect of High Temperature-High Pressure Treatment on Microstructure and Mechanical Properties of Cu-Cr Alloy

First-principle Studies on the Mechanical, Thermodynamic and Electronic Properties of Β″-Mg3gd and Β′-Mg7gd Alloys under Pressure

The Pressure Dependence of the Structure and Superconducting Transition Temperature of Mgb2

Effect of Sintering Time on Superconductivity in Mgb2

High Critical Current Density of a MgB 2 Bulk Superconductor High-pressure Synthesized Directly from the Elements

Investigation of Hot Press and Cold Press Effects on Structural, Electrical and Magnetic Properties of Pyrene Added Bulk MgB2

Ultrasound Studies of Mgb2 Superconductor under Hydrostatic Pressure

Study on the most effective pressure application method to increase the critical temperature of MgB2

High-Pressure and High-Temperature Synthesis of Mgb2 and Its Superconductivity

What High Pressure Studies Have Taught Us about High-Temperature Superconductivity

Improved Superconducting Properties in Bulk MgB2 Prepared by High Energy Milling of Mg and B Powder

SUPERCONDUCTING MgB2 FILMS VIA EX-SITU ANNEALING UNDER DIFFERENT Ar PRESSURE PREPARED BY E-BEAM EVAPORATION

EFFECT OF SINTERING TIME ON SUPERCONDUCTIVITY IN <font>MgB</font><sub>2</sub>

The Influence of Synthesis Parameters on Microstructures and Superconducting Properties of MgB2 Bulks

Simulation of structural parameters and superconducting transition temperature of MgB2 under pressure