Abstract:The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT measurement). The MgB2 phase is identified to form within the temperature range of 430 to 490 C, which is much lower than that with the MgB2 sample fabricated in the same gas environment using the micron-sized magnesium powder, denoted as Micro-MgB2, reported previously. The sample density of the Nano-MgB2 reaches 1.7 g/cm3 with a crystal porosity structure less than a micrometer, as determined by the scanning electron microscope (SEM) images, while the Micro-MgB2 has a much more porous structure with corresponding density of 1.0 g/cm3. This indicates that the Mg raw particle size, besides the sintering temperature, is a crucial factor for the formation of high density MgB2 sample, even at the temperature much lower than that of the Mg melting, 650 C. The X-ray diffraction (XRD) pattern shows a good MgB2 phase with small amount of MgO and Mg and the transition temperature, TC, of the Nano-MgB2 was determined as 39 K by the temperature dependent magnetization measurement (M-T), indicating the existence of a good superconducting property.

High-Pressure and High-Temperature Synthesis of Mgb2 and Its Superconductivity

High-Pressure Synthesis of Mgb2 Superconductor with T-C above 39 K

Structural and Thermodynamic Properties of MgB2 from First-Principles Calculations

Superconducting Properties of MgB 2 Prepared by High Pressure and Ambient Pressure

High Critical Current Density of a MgB 2 Bulk Superconductor High-pressure Synthesized Directly from the Elements

Study of high temperature resistivity and thermal stability of superconductor MgB2

Preparation And Characterization Of The New Superconductor Mgb2

Simulation of Structural Parameters and Superconducting Transition Temperature of Mgb2 under Pressure

The Pressure Dependence of the Structure and Superconducting Transition Temperature of Mgb2

Low Temperature Synthesis of MgB2

Preparation and Characterization of the New Superconductor MgB 2

Phase formation of polycrystalline MgB2 at low temperature using nanometer Mg powder

Potential high-Tc superconductivity in ZrB2 polymorph under pressure

High-density MgB 2 superconducting bulk samples prepared at ambient pressure

Improved superconducting properties of MgB2

Electronic Structure And Superconductivity In Hexagonal Li3b2 And Li2b2h Phases Under Pressure

Simulation of Structural Parameters and Superconducting Transition Temperature of MgB<sub>2</sub> under Pressure

Influences of Heat Treatment and Doping on Microstructure and Superconducting Properties of MgB2 Superconductor

Superconducting Properties of Combustion Synthesized MgB2

Ultrasound Studies of Mgb2 Superconductor under Hydrostatic Pressure