Abstract:In current work, Cu-20wt%W (Cu-20W) composite of near theoretical density (99.69 %) and high electrical conductivity (86.78 %IACS) was fabricated by spray drying technique and hot isostatic pressing (HIP), aiming to enhance the mechanical properties of Cu-W composite while maintaining high conductivity. The impacts of W nanoparticles on the microstructure and properties of Cu-20W samples were evaluated. Adding W nanoparticles can remarkably refine the grain of Cu and strengthen the Cu-W composite through a pinning effect. Room temperature tensile strength and compressive yield strength of Cu-20W composite were 380 MPa and 304.49 MPa, which are 117.14 % and 616.95 % higher than that of pure Cu (175 MPa and 42.47 MPa), respectively. Tungsten nanoparticles can promote the high-temperature reliability of Cu-W samples. Tensile strength of pure Cu and Cu-20W sample gradually decreased with increasing test temperature, but the percentage increment of tensile strength increased. The tungsten particles pinned at grain boundaries during hot deformation inhibit recrystallization grain growth and hinder dislocation movement, thereby contributing to the high-temperature properties of Cu-20W composite. The peak stress of Cu-20W sample is 146.60 % higher than pure Cu, even at close to the melting point of Cu (940 °C). The strength of Cu-20W composite is heightened by combining fine-grain strengthening and dispersion strengthening due to the introduced W nanoparticles.

Low temperature co–sintering of tungsten alloy/steel composite structure

Microstructural characteristics, mechanical properties and interfacial formation mechanism of tungsten alloy/steel composite structure fabricated by HIP co-sintering

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Tungsten heavy alloy: Nano-crystallinity and alloying induced low temperature sintering, microstructure and mechanical properties

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Optimisation of sintering parameters for bonding nanocrystalline cemented tungsten carbide powder and solid high strength steel

Microstructure and mechanical properties of liquid–phase sintered W@NiFe composite powders

Effect of bonding process on the microstructures and strength of W/steel joints with a W-Cu-Ni interlayer

Interfacial microstructure and mechanical properties of WC–Co/40Cr joints brazed at low–temperature with Ag–Cu–Ti + Sn novel filler

Tungsten/steel diffusion bonding using Cu/W–Ni/Ni multi-interlayer

Effects of sintering temperature on interface microstructure and element diffusion of WC-Co-Ni-Fe/high-speed steel composites

Novel low temperature derived W f /W-ZrC-Cu composites by reactive infiltration with enhanced mechanical and thermal physical properties

A low-temperature joining technology suitable for high-temperature applications developed by establishing chemical potential and supercooling gradients

Effects of Holding Time on the Sintering of Cemented Tungsten Carbide Powder and Bonding with High-Strength Steel Wire

SPS Sintering & Joining Based on Preparation of Tungsten-Molybdenum Composite Target

Research on hot isostatic pressing sintering behavior of 90W-Ni-Fe-Cu alloy

Inducing Low-Temperature Melting of TiNiCuNb Eutectic Alloy for Manufacturing Strong C/C-SiC Composite Joints

Fabrication and Characterization of Tungsten Heavy Alloys with High W Content by Powder Metallurgy

Interfacial microstructure and mechanical properties of tungsten alloy/steel diffusion bonding joint using CrFeCoNiCu high entropy alloy interlayer

Research on hot isostatic pressing sintering behavior of 90W–Ni–Fe–Cu alloy

Microstructure and Properties of W Cu Composites with Low Copper Content at Different Sintering Temperatures