Investigation on high strain rate response of lightweight sandwich panel with aluminum corrugated core and smart composite facesheets

S. M. R. Khalili,R. Maher,P. Mahajan

DOI: https://doi.org/10.1007/s40430-023-04669-x

IF: 2.361

2024-01-23

Journal of the Brazilian Society of Mechanical Sciences and Engineering

Abstract:This study investigates experimentally and numerically the performance of lightweight sandwich panels with trapezoidal aluminum corrugated core and composite facesheets reinforced with shape-memory alloys (SMAs) subjected to high strain rate loading. Composite and aluminum samples were prepared to conduct tensile tests, and the requisite data have been obtained during the tests. The composite laminate facesheets made of glass/epoxy were fabricated utilizing the hand-layup approach using 4 layers. For the purpose of reinforcing the composite facesheets, superelastic SMA wires were utilized in three different conditions: 6 SMA wires in the absence of pre-strain, 6 SMA wires with 3 percent pre-strain, and 12 SMA wires with 0 percent pre-strain. The samples were subjected to a high strain rate loading. With the aim of validating and comparing the experimental and numerical results, the samples were modeled in LS-Dyna software, assuming the test condition. This study aims to investigate the influence of adding SMA wires, the quantity and position of SMA wires, and pre-straining the SMA wires in the composite facesheets to enhance the performance of sandwich panels against the high strain rate loadings. The presence of SMA wires results in better energy absorption and the employment of pre-strain results in better high strain rate behavior in sandwich panel at the expense of its weight. The results demonstrate that the absorbed energy from 117.247 J for the samples without the SMA wire was increased to 128.749 J for the 6 SMA wires samples. However, when a pre-strain of 3% was applied to the wires, the energy absorption in the samples with 6 SMA wires increased further to 142.57 J. On the contrary, when the SMA wires were located far from the center of the hitting point, the energy absorbed decreased to 123.12 J for the samples with 12 wires without pre-strain.

engineering, mechanical