Solidification evolution and corrosion performance of CoCrFeNiB x eutectic high entropy alloy coatings
Qi Zhang,Yueqi Si,Bin Han,Meiyan Li,Qin Wang,Wenqi Bian,Xixin Xue
DOI: https://doi.org/10.1016/j.surfcoat.2024.130760
IF: 4.865
2024-04-13
Surface and Coatings Technology
Abstract:CoCrFeNiB x (x = 0.15, 0.30, 0.45, 0.60, 0.75) eutectic high entropy alloy (EHEA) coatings, abbreviated as B0.15–B0.75, were prepared by laser cladding. The inevitability of solid-state phase transition in B0.75 coating has been verified from the perspective of enthalpy. The solidification and crystallization process and laws of the CoCrFeNiB x coatings were obtained by observing the phase and microstructure, combining the DSC testing and analysis. When the mole ratio of B atoms x ≤ 0.45, the FCC1 phase solidifies into dendrites, and the eutectic structure composed of the coupling of FCC1 and FCC2 lamellae forms between dendrites. As the content of B increases, the proportion of eutectic structure rises steadily while the dendrites refine and decrease. When x = 0.60, the B content reaches the eutectic point, forming the eutectic structure with a feathery appearance. When x = 0.75, a strip-shaped boride structure will also precipitate after the formation of the metastable eutectic structure. The B element can promote the formation of eutectic structures, thereby improving the microhardness of the CoCrFeNiB x coatings from 267.0 HV 0.2 to 555.4 HV 0.2 . However, as the B content rises, the corrosion current density of the CoCrFeNiB x coating in 3.5 % NaCl solution decreases from 1.08E−07 A/cm 2 to 8.92E−06 A/cm 2 . The corrosion mechanism changes from pitting corrosion to intergranular corrosion. The high-phase interfacial energy of the eutectic structure exacerbates the galvanic corrosion of the coatings.
physics, applied,materials science, coatings & films