Abstract:In situ reversible CO 2 capture by thermally stable materials such as oxides has drawn much attention because of the high operation temperatures of the main CO 2 sources, namely thermal power plants and internal combustion engines. In particular, Li 4 SiO 4 features a high CO 2 absorption capacity but suffers from slow CO 2 absorption at practical CO 2 partial pressures ( P (CO 2 )), which can be mitigated through the incorporation of Na to afford Li 3 NaSiO 4 . Given that the Li 3 NaSiO 4 regeneration kinetics and the possibility of the corresponding absorption/desorption cycling based on temperature or P (CO 2 ) control remain underexplored, we herein characterized Li 3 NaSiO 4 as a material for reversible CO 2 absorption at high temperatures in response to CO 2 /N 2 gas switching, achieving excellent cycling performance at 750 °C. CO 2 desorption (i.e., Li 3 NaSiO 4 regeneration) was concluded to occur at the interface between solid Li 2 SiO 3 and molten LiNaCO 3 , generating a Li 3 NaSiO 4 layer that prevented further desorption at a thickness of > 1 μm and thus resulted in the saturation of the CO 2 desorption reaction in the middle. The lack of such saturation during cycling was attributed to the formation of needle-like (short side length ≈ 2 μm) Li 2 SiO 3 particles upon the absorption of CO 2 by Li 3 NaSiO 4 . Thus, this work paves the way for the development of industrially applicable high-temperature CO 2 capture/release materials and thus contributes to the establishment of a greener society.

Li3NaSiO4 as reversible CO2 absorbent: elucidation of performance-governing factors and regeneration mechanism