Mechanism of low‐temperature brittle‐ductile transition of polypropylene/low‐density polyethylene blend foam under compressive stress caused by cells stretching

Bu-Yong Wu,Ya-Ning Li,Jian-Ming Yang,Ying-Guo Zhou

DOI: https://doi.org/10.1002/adem.202300533

IF: 3.6

2023-05-13

Advanced Engineering Materials

Abstract:Blending with polyethylene (PE) is a conventional way to improve the low‐temperature toughness of polypropylene (PP). However, the mechanical deformation behavior of PP/PE blends at different temperature has not been fully revealed, and the enhancement of low‐temperature toughness was far less than expected. To enhance the low‐temperature toughness of PE/low density polyethylene (LDPE) blends system, which was a crucial blend for polyolefin materials with wide application in frigid regions, the PP/LDPE blend foam samples with stretched cells were fabricated via a facile injection foaming together with open‐mold stretching process. During the open‐mold stretching, the relatively miscible PP and LDPE chains were debonded, and then the stretched and oriented cells structure with lots of tiny inter‐phase cavities between the PP and LDPE phases and the fine lamellae were formed in the blend foam system. Such inter‐phase cavities provided an adequate movement space for the frozen PP and LDPE chains and lamellae, and effectively relaxed and transferred stress, when compressed at ‐25 °C, which greatly promoted the uniform compressive behavior accompanied by the completely compacted cells. Moreover, the compressive fracture surface changed from relatively flat and smooth for the stretched PP foam to obvious yield folds and deformation for the stretched blend foam, and the compressive strain of stretched PP/LDPE blend foam was highly enhanced by a roughly 31%, 53% and 44% increase than that of PP, PP/LDPE and stretched PP foam samples, respectively, achieving the low‐temperature brittle‐ductile transition for PP. This work provides a facile strategy for fabricating PP/LDPE blend with good low‐temperature toughness and promising application potentials. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary