Ti3C2Tx Nanosheet/Bi2S3 Nanobelt Composites for NO2 Gas Sensing
Chong Li,Ran Tao,Jianlei Zhang,Jinlong Chen,Chen Fu,Jikai Zhang,Huiling Ong,Chenze Lu,Yi Chen,Qiang Wu,Jing-Ting Luo,Yongqing Fu
DOI: https://doi.org/10.1021/acsanm.4c01577
IF: 6.14
2024-01-01
ACS Applied Nano Materials
Abstract:Along with the revolution of the Internet of Things (IoT), smart, flexible, easily fabricated, and highly sensitive gas sensors are essential for many portable electronics. In this study, a wearable NO2 sensor based on a nanomesh structure woven with Ti3C2Tx microflakes and Bi2S3 nanobelts operated at room temperature was successfully designed and prepared. The effects of the mass ratio between two materials on the performance were evaluated. Bi2S3 nanobelts embedded inside accordion-like Ti3C2Tx provide large specific surface areas and abundant active sites for the adsorption of NO2 molecules. Attributed to the high conductivity of Ti3C2Tx, the carriers generated in the sensitive layers are easily transmitted during sensing, thus significantly reducing the response and recovery times. The sensor based on the nanomesh containing 30 wt % Ti3C2Tx exhibits excellent sensing performance, fast response/recovery rates, and high stability even in arbitrary deformed shape conditions. Upon exposure to 1 ppm NO2, the response of the sensor is 12.67, and the response/recovery times are 5/28 s, respectively. A stable sensing performance can be maintained after 1500 cycles of deformation. This work demonstrates a simple but reliable manufacturing strategy of wearable gas sensors for the next generation of IoT monitoring network-linking human activities.