Abstract:This present study mainly focuses on the influence of low-calcium circulating fluidized bed fly ash (LCFA) on the mechanical property and microstructure of cement-based materials under different curing conditions. The mechanical properties test was conducted by changing variable parameters, such as LCFA content, the internal mixing ratio of LCFA and fly ash (FA), and dry and water curing conditions. Further, the hydration products and pore structure were analyzed using XRD, FT-IR, TG-DTG, NI, SEM, and BET micro-testing technology. The strength development law of LCFA on cement-based materials is discussed. The research results show that LCFA has a certain degree of self-hardening and can be used as a cementitious material in cement-based materials. Still, the loose and porous microstructure of LCFA leads to higher water requirements, which reduces the fluidity of cement-based pastes. Water curing is favorable for promoting the development of LCFA on the long-term compressive strength of cement-based materials. When the LCFA was added to the cement, the optimal substitution ratio was 20%, and the compressive strength at 91 days reached 101 MPa. In the case of compounding LCFA and FA, when the internal mixing ratio of LCFA/FA was 3 and the total content was 20%, the mechanical properties were the highest, and the compressive strength at 91 days was 92 MPa. The microscopic analysis result shows that the cumulative hydration heat of the samples decreased significantly with the increase of dosage of LCFA. The main hydration products of cement-based materials mixed with LCFA were AFt, C-S-H gel, and Ca(OH)2. AFt and C-S-H gels are critical to the strength development of OPC-LCFA samples. The active Al2O3 and active SiO2 in LCFA were involved in hydration reactions to promote the formation of C-A-H and C-S-H gel and effectively promote the development of the mechanical properties. Overdosages of LCFA would reduce the ettringite formation rate. FA is not conducive to AFt formation in the hydration process of OPC-FA samples.

Hydration and Mechanical Properties of High-Volume Fly Ash Cement under Different Curing Temperatures

Compressive Strength Development of High-Volume Fly Ash Ultra-High-Performance Concrete under Heat Curing Condition with Time

Hydration, mechanical properties and durability of high-strength concrete under different curing conditions

Influence of Fly Ash on the Compressive Strength of Concrete under Temperature Match Curing Conditions

Effects of Fly Ash Particle Size and Chemical Activators on the Hydration of High-Volume Fly Ash Mortars

Effects of Mixing and Curing Temperature on the Strength Development and Pore Structure of Fly Ash Blended Mass Concrete

The Effects of Curing Temperature on CH-Based Fly Ash Composites

Study on Mechanical and Microscopic Properties of Fly Ash Cement-Based Materials in High Geothermal Environment

Effect of Curing Conditions on Property of High Performance Concrete with Composite Mineral Admixture

The Relationship of Compressive Strength and Chemically Bound Water Content of High-Volume Fly Ash-Cement Mortar

Investigation of Low-Calcium Circulating Fluidized Bed Fly Ash on the Mechanical Strength and Microstructure of Cement-Based Material

Evaluation of early-age thermal cracking resistance of high w/b, high volume fly ash (HVFA) concrete using temperature stress testing machine

Influence of Steam Curing Method on the Performance of Concrete Containing a Large Portion of Mineral Admixtures

Influence Mechanism of Initial Concreting Temperature and Water-Binder Ratio on Hydration Rate of Fly Ash Concrete

Investigating the Impact of Fly Ash on the Strength and Micro-Structure of Concrete during Steam Curing and Subsequent Stages

The difference among the effects of high-temperature curing on the early hydration properties of different cementitious systems

Fresh, Durability and Mechanical Behavior of Self Consolidating Concrete Incorporating Fly Ash and Admixture under Hot Weather

Effects of high temperature and post-fire-curing on compressive strength and microstructure of calcium carbonate whisker-fly ash-cement system

Effects of different curing regimes on the compressive strength properties of self compacting concrete incorporating fly ash and silica fume

Performance of concrete containing fly ash at early ages

Impact of Hot Weather Conditions on the Performance of Supplementary Cementitious Materials Concrete