Abstract:Objective:To investigate the effect of titanium tetrafluoride (TiF 4) solution on bonding strength of acid-etched dentin. Methods:Tooth crown dentin proximal to the pulp cavity was obtained from 24 freshly-extracted human third molars and randomly divided into 6 groups ( n=4 each) . Among them, 4 groups were modeled for artificial acid-etched dentin by means of acid-etching and mechanical friction. The other 2 groups were used as sound dentin controls. One each of the artificial acid-etched dentin groups and sound dentin control groups were randomly selected and studied under scanning electron microscope and microhardness tester to measure the surface morphology and hardness, and to evaluate the effectivity of the modeling for artificial acid-etched dentin. The other 3 groups of artificial acid-etched dentin and remaining group of healthy dentin were used for bonding test, re-assigned into 4 groups according to different treatments: etched dentin treated with 4.0% TiF 4 (4.0% TiF 4-ED group) , etched dentin treated with 2.5% TiF 4 (2.5% TiF 4-ED group) , untreated etched dentin (ED group) and sound dentin control (SD group) . All dentin samples were then bonded with a self-etching system (SE bond) , layered by AP-X composite resin with light-curing. Microtensile bonding strength (μTBS) test was used to measure the immediate bonding strength and to determine the fracture pattern. Results:The microhardness values of artificial acid-eched dentin and sound dentin were (56.92±5.27) HV and (60.19±4.52) HV, respectively, with significant difference between groups ( P<0.05) . Scanning electron microscopy confirmed that the artificial acid-etched dentin presented microscopic morphological characteristics consistent to natural acid etching. The μTBS of 4.0% TiF 4-ED group, 2.5% TiF 4-ED group, ED group and SD group were (28.94±8.04) MPa, (46.08±8.19) MPa, (20.39±7.46) MPa and (45.16±7.86) MPa, respectively. The μTBS did not differ significantly between the 2.5% TiF 4-ED group and the SD group ( P=0.529) , and both were higher than those in the 4.0% TiF 4-ED group and the ED group (all P<0.05) . The fracture patterns differed significantly among the 4 groups ( χ2=54.91, P<0.001) . In the 2.5% TiF 4-ED group, cohesive dentin fracture was the main cause, suggesting that the bonding strength may be higher than the mean measurements from the micro-tensile test. Conclusion:The bonding strength of acid-etched dentin is lower compared with sound dentin. 2.5% TiF 4 solution can significantly improve the bonding strength of acid-etched dentin.

Study on the adverse effect of acid-corrosion on the dentin in terms of degradation of fracture resistance

Influence of Casein Phosphopeptide-Amorphous Calcium Phosphate Application, Smear Layer Removal, and Storage Time on Resin-Dentin Bonding

The influence of caries-affected dentin on bonding effect of deciduous teeth

A Numerical Study of Crack Penetration and Deflection at The Interface Between Peritubular and Intertubular Dentin

Effect of Polyphenols on the Ultrastructure of the Dentin Pellicle and Subsequent Erosion

The effect of different conditioning agents on dentin roughness and collagen structure

The Enamel Softening and Loss During Early Erosion Studied by Afm, Sem and Nanoindentation

Post-failure analysis of model resin-composite restorations subjected to different chemomechanical challenges

The effect of thermocycling and dentine pre-treatment on the durability of the bond between composite resin and dentine.

Effect of surface treatments on fracture resistance of root filled teeth with bonded fibre posts

Effect of titanium tetrafluoride solution on bonding strength of acid-etched dentin

Improvement of acid resistance of Zn-doped dentin by newly generated chemical bonds

Effect of an extrafibrillar dentin demineralization strategy on the durability of the resin–dentin bond

Microhardness and energy dispersive X-ray evaluation of dentinal walls following chemical and electrochemical dissolution of fractured nickel-titanium file: An in vitro study

Preliminary Exploration of a Laser-Based Surface Microtexturing Strategy for Improving the Wear Resistance of Dentin: an in Vitro Study.

Effects on different full-coverage designs and materials of crack propagation in first mandibular molar: an extended finite element method study

Biomechanical perspectives on dentine cracks and fractures: Implications in their clinical management

Effect of phosphoric acid containing polyvinylpyrrolidone as protective etchant for dentin bonding

Effect of Chemical Removal or Mechanical Modification of Smear Layer on Dentin Adhesion with Universal Resin Adhesives

A Scanning Electron Microscope Evaluation of the Efficacy of Different Fluoride-releasing Dental Restorative Materials to Prevent Enamel Demineralization: An In Vitro Study

Development of TiF4-Dendrimer complex gel as an anti-demineralization agent for dentin: An in vitro study