Interdiffusion Studies in Alloy 617 and 10Cr Steel Joints Using Diffusion Couple Approach and Simulations

S. Haribabu,C. Sudha,P. Ganesh,Abhay Kumar

DOI: https://doi.org/10.1007/s11669-024-01118-7

2024-05-23

Journal of Phase Equilibria and Diffusion

Abstract:In the steam turbine circuit of advanced ultra supercritical power plants dissimilar joints of alloy 617 and 10Cr steel are unavoidable due to economic reasons. In these joints diffusional interaction causing change in microstructure is identified as possible reason for failure during service. To investigate the interdiffusion driven structural changes, alloy 617/10Cr steel diffusion couples were fabricated. To achieve good metallurgical bond between Fe- and Ni-based alloys and to study diffusional transformations under accelerated conditions, diffusion couples were prepared by annealing in the temperature range of 1000-1100 °C for 3-8 h. For all conditions heat treatment interaction zones were wider in alloy 617 (150-200 μm at 1050 °C, 8 h) than in 10Cr steel (15-16 μm at 1050 °C, 8 h) and the phase stability at the interface was studied using electron microprobe and x-ray diffraction. Average effective interdiffusion coefficients were calculated using Dayananda's approach. While the diffusivities of substitutional solutes were similar in alloy 617 (0.31-0.42 × 10 −15  m 2 /s at 1050 °C), they differed in 10Cr steel in the following sequence: > ≈ > Further, multicomponent interdiffusion profiles were predicted using homogenization model in DICTRA and an integrated approach combining DICTRA with Thermo-Calc helped in understanding the experimental observations on the interface microstructure.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

### Problems the Paper Attempts to Solve

The paper primarily explores the interdiffusion phenomenon and its impact on the microstructure of heterogeneous joints between Alloy 617 and 10Cr steel under high-temperature conditions. Specifically, the study aims to:

1. **Understand the microstructural changes in the interface region**: In advanced ultra-supercritical (AUSC) coal-fired power plant steam turbine circuits, the use of joints made from different materials is inevitable due to economic reasons. The diffusion interactions in these joints may lead to failure during service. Therefore, the study investigates the structure changes driven by interdiffusion by preparing Alloy 617/10Cr steel diffusion couples.

2. **Evaluate the interdiffusion coefficients**: The average effective interdiffusion coefficients are calculated from experimental data, and the multicomponent interdiffusion process is simulated using DICTRA software to better understand the microstructural changes in the interface region.

3. **Validate the simulation results**: The DICTRA simulation results are compared with experimental observations to verify the effectiveness of the simulation method and to reveal the challenges in practical applications.

Through these studies, the paper aims to provide a theoretical foundation and technical support for the future design of more high-temperature and high-pressure resistant material joints.