Novel and durable composite phase change thermal energy storage materials with controllable melting temperature
Haiting Wei,Shuiyuan Yang,Cuiping Wang,Changrui Qiu,Kairui Lin,Jiajia Han,Yong Lu,Xingjun Liu
DOI: https://doi.org/10.1016/j.jmst.2020.12.071
IF: 10.319
2021-09-01
Journal of Materials Science and Technology
Abstract:Novel and durable Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN with tunable melting temperature were prepared.The Al-Si alloy and Al<sub>2</sub>O<sub>3</sub> shell were prepared by the reaction of SiO<sub>2</sub> with melted Al.The shell crack repaired itself by nitriding of melted Al to form Al<sub>2</sub>O<sub>3</sub>-AlN shell.The Al<sub>2</sub>O<sub>3</sub>-AlN shell can obviously improve the thermal stability of composite PCM.The Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN can be used in thermal storage systems for more than 6 years.The development of high temperature phase change materials (PCMs) with great comprehensive performance is significant in the future thermal energy storage system. In this study, novel and durable Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN composite PCMs with controllable melting temperature were successfully synthesized by using pristine Al powder as raw material and tetraethyl orthosilicate as SiO<sub>2</sub> source. The Al<sub>2</sub>O<sub>3</sub> shell and Al-Si alloy were in-situ produced via the substitution reaction between molten Al and SiO<sub>2</sub>. Importantly, the crack caused by the incomplete encapsulation of the Al<sub>2</sub>O<sub>3</sub> shell could repair itself by the nitridation reaction of internal molten Al and thereby forming a highly dense Al<sub>2</sub>O<sub>3</sub>-AlN composite shell. The produced dense Al<sub>2</sub>O<sub>3</sub>-AlN composite shell could significantly improve the thermal cycling stability of composite PCMs, and thus, the thermal storage density decrease of the Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN (59.8 J/g to 77.7 J/g) was far less than that of the Al-Si/Al<sub>2</sub>O<sub>3</sub> (118.5 J/g) after 3000 thermal cycles. Moreover, the synthesized Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN still exhibited a controllable melting temperature (571.5‒637.9 ℃), relatively high thermal storage density (105.6‒150.7 J/g), great dimensional stability and structural stability after 3000 thermal cycles. Hence, the synthesized Al-Si/Al<sub>2</sub>O<sub>3</sub>-AlN composite PCMs, as promising preferential thermal energy storage materials, can be stably used in the energy utilization efficiency improvement of various systems for more than 6 years.<span class="display"><span><ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1005030221001456-fx1_lrg.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download high-res image (89KB)</span></span></a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1005030221001456-fx1.jpg"><span class="anchor-text">Download : <span class="download-link-title">Download full-size image</span></span></a></li></ol></span></span>
materials science, multidisciplinary,metallurgy & metallurgical engineering