Abstract:The failure of fiber-reinforced ceramic and metal matrix composites under a fixed load for extended times occurs because of strength degradation in the constituent fibers. Specifically, the ceramic fibers possess a Weibull strength distribution caused by crack-like flaws, which can grow according to a power-law growth mechanism. Failure of individual fibers causes interfacial slippage and stress redistribution to unfailed fibers, which in turn accelerates the degradation rate of the remaining fibers, and culminates in abrupt failure of the composite after sufficient damage has accumulated. This sequence of events is modeled both analytically and numerically within the Global Load Sharing (GLS) approximation previously utilized for quasi-static loading. Analytically, a general constitutive model for the relationship between the stress on the damaged fiber bundle, the strain in the unbroken fibers, and the extent of damage, is combined with a time-dependent damage evolution equation derived from the slow-crack-growth kinetics to yield an integral equation for the strain vs time at fixed applied load. The relevant gauge length for a fixed-load rupture process is found to be δ = rστ which is twice the slip length prevailing at the initial applied load σ, where τ is the interfacial sliding resistance between fiber and matrix. The underlying time scale for rupture is the time scale for a typical fiber of gauge length δ to fail under the applied load σ; this time can be quite different from that measured by stress-rupture tests on single fibers at an unrelated laboratory gauge length L0. A simple, accurate but approximate relationship between applied load, time to failure, fiber Weibull modulus, and slow crack growth exponent is presented. The numerical simulations of the same degradation process verify the general accuracy of the failure time obtained from the analytic results. The remaining tensile strength after some time at load but prior to failure is also studied, and the simulation results generally exhibited a more sudden-death failure than the analytical predictions. A specific application to the failure of a Nicalon fiber composite is presented.

Subcritical crack growth in fibrous materials

Slow crack growth : models and experiments

Slow crack growth in polycarbonate films

A dynamical law for slow crack growth in polycarbonate films

The Crack Growth Resistance of Polymeric Cellular Materials Studied With a Quasi‐Brittle Approach

Scaling behaviour in the fracture of fibrous materials

A mesoscopic approach to subcritical fatigue crack growth

Understanding fast macroscale fracture from microcrack post mortem patterns

Computational Monitoring of an Initial Fatigue Crack Incubation and Growth in a Smooth Specimen

Power law creep and delayed failure of gels and fibrous materials under stress

The Role of Surface Forces in Environment-Enhanced Cracking of Brittle Solids

Cracks in random brittle solids: From fiber bundles to continuum mechanics

A Multiscale Crack-Bridging Model of Cellulose Nanopaper

Crack Front Segmentation and Facet Coarsening in Mixed-Mode Fracture

Crack path instabilities in DCDC experiments in the low speed regime

A steady-state frictional crack in a strip

Time-dependent failure in fiber-reinforced composites by fiber degradation

The effect of fibre orientation on fatigue crack propagation in CFRP: Finite fracture mechanics modelling for open-hole configuration

Facet formation in slow three-dimensional fracture

Crack Growth in Rotor P2M Steel at Elevated Temperature