All sprayed fluorine-free membrane electrode assembly for low-platinum and low-humidity proton exchange membrane fuel cells

Weisheng Yu,Xiaoqi Yang,Xian Liang,Yan Xu,Xianhe Shen,Xiaolin Ge,Liang Wu,Tongwen Xu

DOI: https://doi.org/10.1039/d3ta00603d

IF: 11.9

2023-03-23

Journal of Materials Chemistry A

Abstract:Reducing platinum catalyst loading and humidity dependence of the membrane electrode assemblies (MEAs) is highly desirable for commercializing proton exchange membrane fuel cells (PEMFCs). Meanwhile, replacing the perfluorinated sulfonic-acid PEMs with fluorine-free hydrocarbon membranes can reduce manufacturing costs. We present an all spraying (AS) method to fabricate a fluorine-free hydrocarbon-based MEA (AS-MEA). Such an MEA achieves a much higher H2/O2 fuel cell performance than the conventional catalyst-coated substrate MEA (CCS-MEA). The peak power density is 1.6 W cm-2 for the AS-MEA vs. 1.2 W cm-2 for the CCS-MEA with 100% relative humidity (RH) and 0.1/0.1 L min-1 H2/O2 and 0.1 MPa backpressure gas feeds. More importantly, the performance superiority is particularly prominent at low RH and catalyst loading. The AS-MEA achieves a competitively peak power density of 0.6 W cm-2 at 40% RH with a low Pt loading of 0.1 mg cm-2, which is more than 3-fold that of the CCS-MEA. Equivalent-circuits-based analyses of the electrochemical impedance spectroscopy show that the exceptional performance arises from the tightly integrated PEM–catalyst layer boundary, as confirmed by the cross-sectional morphological investigations. Moreover, the AS-MEA shows appreciable in-situ durability during a 100 h of accelerated stress test.

materials science, multidisciplinary,chemistry, physical,energy & fuels