Abstract:In the present study, porous TiO2 foams (PTF) were prepared by particle-stabilized emulsion method. The samples having solid contents ranging from 20 wt.% to 35 wt.% were prepared and successfully impregnated with paraffin without using a surfactant. SEM images showed that the prepared PTFs had three-dimensional interpenetrating structures with good porosities. The pore structure and morphology of PTF was markedly influenced by the solid content. With increase in solid content, porosity decreased, along with a decrease in the homologous encapsulation ratio of paraffin. Differential scanning calorimetry (DSC) evaluated the thermal properties of the paraffin/PTF (PTFP) composites. DSC results showed that with a solid content of 20 wt.%, the paraffin adsorption reached 62 vol.% and latent heat of the composite PCM was 94.05 Jig after 200 melting/freezing cycles. TGA results showed that the form-stable composite PCMs had good thermal stabilities. In order to further enhance the thermal conductivity and improve the adsorption capacity of PTF, sucrose was added to the emulsion and carbonized in situ to form carbon/PTF (PTFC). This could also be successfully impregnated with paraffin to obtain the form-stable composite paraffin/PTFC (PTFCP). The TEM images and results of XPS analysis confirmed that the surfaces of TiO2 particles were covered with a 2 nm thick carbon film (C/TiO2). The thermal conductivity of PTFCP increased from 0.302 W/m K to 1.059 W/m K compared to PTFP, along with a further improvement in adsorption capacity. Furthermore, the results of FT-IR analysis and thermal cyclic tests showed that the form-stable composite PCMs had good chemical stability and thermal reliability after 200 melting/freezing cycles. Therefore, the prepared form-stable composite PCMs having excellent pore structures, thermal properties, thermal reliabilities, and chemical stabilities are promising PCM candidates for heat energy storage applications. (C) 2016 Elsevier Ltd. All rights reserved.

Paraffin wax with an addition of nano Ti2O3: Improve thermal and photothermal performances with little decreased latent heat

Research on the modification of microencapsulated phase change material for thermal energy storage by nano-SiO2 and graphite

Thermal Energy Storage Performance of Paraffin-Based Composite Phase Change Materials Filled with Hexagonal Boron Nitride Nanosheets

Thermophysical Properties of Paraffin-Based Composite Phase Change Materials Filled with Carbon Nanotubes

Thermophysical Properties of a Novel Nanoencapsulated Phase Change Material

Experimental Investigation of Photothermal Properties of Phase Change Material Enhanced by Zn–TiN Binary Nanoparticles

Investigation on the Melting Performance of a Phase Change Material Based on a Shell-and-Tube Thermal Energy Storage Unit with a Rectangular Fin Configuration

Photothermal properties and photothermal conversion performance of nano-enhanced paraffin as a phase change thermal energy storage material

Enhanced thermal energy storage of a paraffin-based phase change material (PCM) using nano carbons

Superior Thermal Conductivity and Charging Performance of Zinc Oxide Dispersed Paraffin Wax for Thermal Energy Storage Applications

Experimental investigation on photothermal properties of Zn–ZnO/paraffin hybrid nanofluids

Thermal characteristics enhancement of Paraffin Wax Phase Change Material (PCM) for thermal storage applications

Enhancing the performance of thermal energy storage by adding nano-particles with paraffin phase change materials

Thermo-physical properties of paraffin wax with iron oxide nanoparticles as phase change material for heat storage applications

Thermal Property Enhancement of Paraffin-Wax-Based Hydroxyl-Terminated Polybutadiene Binder with a Novel NanoSiO(2)-Expanded Graphite-PW Ternary Form-Stable Phase Change Material

The Experimental Exploration of Nano-Si3n4/paraffin on Thermal Behavior of Phase Change Materials

Nano Engineered Paraffin-Based Phase Change Material for Building Thermal Management

Binary composite (TiO2-Gr) based nano-enhanced organic phase change material: Effect on thermophysical properties

Preparation of Paraffin/porous TiO2 Foams with Enhanced Thermal Conductivity As PCM, by Covering the TiO2 Surface with a Carbon Layer

Molecular Dynamics Simulation of Nanoparticle Effect on Melting Enthalpy of Paraffin Phase Change Material

Enhancing the solar absorption capacity of expanded graphite-paraffin wax composite phase change materials by introducing carbon nanotubes additives