Thermophysical Properties of Paraffin-Based Composite Phase Change Materials Filled with Carbon Nanotubes

王晓,丁晴,姚晓莉,方昕,范利武,徐旭,俞自涛,胡亚才

DOI: https://doi.org/10.3969/j.issn.1671-8097.2013.02.006

2013-01-01

Journal of Thermal Science and Technology

Abstract:Paraffin-based nanocomposite phase change materials(PCMs)with various mass fractions(1% ～5%)were prepared using multi-walled carbon nanotubes(MWCNTs)as the fillers.The phase change behaviors of the composite PCMs were characterized by employing the differential scanning calorimetry technique,whereas the thermal conductivity was measured using the transient hot-wire method.It was shown that although the phase change temperatures of the composite PCMs is almost constant,their phase change enthalpy almost linearly decreases with increasing loading of the MWCNTs.The phase change enthalpy is lowered by approximately 15%as compared to that of pure paraffin at a mass fraction of 5%.The thermal conductivity of the composite PCMs was found to decay fairly with elevating temperature,except for 30and 50℃at which a sudden increase was seen due to the solid-solid and solid-liquid phase change,respectively.In addition,thermal conductivity was shown to increase linearly with raising mass fraction.At the mass fraction of 5%,the relative thermal conductivity enhancement is nearly 40%.