Abstract:In this study, a novel sol-gel method is used to synthesize amorphous silica-alumina materials with a narrow mesoporous distribution and various Si/Al molar ratios without using any templates and pore-regulating agents. During the preparation procedure, only inexpensive inorganic salts were used as raw materials, instead of expensive and harmful alkoxides. The precursor sol was dried at room temperature in a vacuum box kept at 60 mmHg until it began to form the gel. The results of a nitrogen sorption experiment indicate that the synthesized materials with different Si/Al molar ratios have similar mesoporous distributions (within 2-12 nm). Moreover, it was found that the material's pore size distribution remains at a similar value during the heat treatment from room temperature to 550 degreesC. On the basis of the nitrogen sorption, TEM, and AFM characterization results, a formation mechanism of mesopores which accounts for the experimental data is also suggested. This suggested mechanism involves rearrangement of the primary particles during the drying process to form the precursors of the similarly sized mesopores. The synthesized materials were characterized by XRD, thermal analysis (TG/DTA), Al-27 and Si-29 MAS NMR spectroscopy, SEM, TEM, and AFM. The results of Al-27 and 29Si MAS NMR indicate that the distribution of silicon and aluminum in the synthesized materials is more uniform and homogeneous than that in the mixed oxides prepared via the traditional sol-gel method even at high alumina contents. The type and density of the acid sites were studied using pyridine adsorption-desorption FTIR spectroscopy. It was shown that the acidity of the synthesized materials is higher than that of the silica-alumina materials prepared by conventional methods.

Modification of the pore structure of sol-gel-derived ceramic oxide powders by water-soluble additives

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Design of nanosized structures in sol-gel derived porous solids. Applications in catalyst and inorganic membrane preparation

Synthesis of Mesoporous Silica Using the Sol-Gel Approach: Adjusting Architecture and Composition for Novel Applications

The Influences of Additives on the Zirconia Sol-Gel

Preparation and properties of porous ceramics based on alumomagnesium spinel and zirconium dioxide

A Novel Method To Synthesize Amorphous Silica−Alumina Materials with Mesoporous Distribution without Using Templates and Pore-Regulating Agents

Synthesis of Mesoporous Tetragonal ZrO2, TiO2 and Solid Solutions and Effect of Colloidal Silica on Porosity

The effect of adding PDMS-OH and silica nanoparticles on sol-gel properties and effectiveness in stone protection

Preparation and Characterization of Al<sub>2</sub>O<sub>3</sub>-Based Composite Membranes by Sol-Gel Method

Sol-gel preparation of ZrO2–Li2Si2O5 ceramics and their sintering properties

Highly Porous and Mechanically Robust Al2O3-based Foams with Self-Wrinkled and Rough Aperture Surfaces Via Binary Colloidal Self-Assembly of Nanoparticle/gelation Network

Sol–gel Synthesis of Mesoporous Spherical Zirconia

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Ceramics by the Solution-Sol-Gel Route

A novel sintering additive system for porous mullite-bonded SiC ceramics: High mechanical performance with controllable pore structure

Postsynthetic modification of yttria‐stabilized zirconia aerogels with silica coatings for enhanced thermal stability

Synthesis, Densification and Characterization of Nanosized Oxide Ceramic Powders with Eutectic Compositions by Heating of Alcohol-Aqueous Salt Solutions

Porous MgO-based ceramics synthesized by the volume expansion effect: Designing and performance