Ternary diffusion in the α and γ phases of the Fe-Ni-P system

T. R. Heyward,J. I. Goldstein

DOI: https://doi.org/10.1007/bf02669372

1973-10-01

Metallurgical Transactions

Abstract:Ternary diffusion coefficients have been determined in the α-bcc and γ-fcc phases of the Fe-Ni-P system and at four temperatures 1200, 1100, 1000, and 900°C. At 1100°C the ratio ofDNiNiFe/DPPFein the α phase is 0.3 to 0.4 and the ratio of the cross coefficientDPNiFe/DPPFe is 0.03 to 0.05. m the γ phase the corresponding ratios are 0.01 to 0,02 and 0.0015 to 0.0025. The other cross coefficientDNiPFe could not be evaluated because of experimental uncertainties. Estimates of the ratioDNiPFe/DNiNiFe using the interaction parameter ε12 are 0.004 to 0.01 in the α phase and 0.02 to 0.04 in the γ phase. The addition of P in both the α and γ phase increases the major ternary coefficients up to as much as a factor of ten at one temperature. This is consistent with the fact that P lowers the melting point of FeNi in the ternary system, up to 500°C. Isodiffusion coefficient contours obtained at 1100°C plot approximately parallel to the α and γ solidus boundaries and are similar in shape to the α and γ solidus boundaries as a function of temperature. Activation energies andD0 values were computed at selected compositions in both α and γ phases forDPPFe andDNiNiFeand are given below: