Abstract:In this paper, the effect of thermomechanical treatment process on the hardening behavior, grain microstructure, precipitated phase, and tensile mechanical properties of the new high-strength and high-ductility Al-10.0Zn-3.0Mg-2.8Cu alloy was studied, and the optimal thermomechanical treatment process was established. The strengthening and toughening mechanisms were revealed, which provided technical and theoretical guidance for the engineering application of this kind of high strength-ductility aluminum alloy. Al-10.0Zn-3.0Mg-2.8Cu alloy cylindrical parts with external longitudinal reinforcement were prepared by a composite extrusion deformation process (reciprocal upsetting + counter-extrusion) with a true strain up to 2.56, and the organizational evolution of the alloys during the extrusion deformation process and the influence of pre-stretching treatments on the subsequent aging precipitation behaviors and mechanical properties were investigated. The results show that firstly, the large plastic deformation promotes the fragmentation of coarse insoluble phases and the occurrence of dynamic recrystallization, which results in the elongation of the grains along the extrusion direction, and the volume fraction of recrystallization reaches 42.4%. Secondly, the kinetic study showed that the decrease in the activation energy of precipitation increased the nucleation sites, which further promoted the diffuse distribution of the second phase in the alloy and a higher number of nucleation sites, while limiting the coarsening of the precipitated phase. When the amount of pre-deformation was increased from 0% to 2%, the size of the matrix precipitated phase decreased from 5.11 μm to 4.1 μm, and when the amount of pre-deformation was increased from 2% to 7%, the coarsening of the matrix precipitated phase took place, and the size of the phase increased from 4.1 μm to 7.24 μm. The finalized heat treatment process for the deformation of the aluminum alloy tailframe was as follows: solution (475 °C/3 h) + 2% pre-stretching + aging (120 °C/24 h), at which the comprehensive performance of the alloy was optimized, with a tensile strength of 634.2 MPa, a yield strength of 571.0 MPa, and an elongation of 15.2%. The alloy was strengthened by both precipitation strengthening and dislocation strengthening. After 2% pre-stretching, the fracture surface starts to be dominated by dense tough nest structure, and most of them are small tough nests, and small and dense tough nests are the main reason for the increase in alloy toughness after 2% pre-stretching deformation.

Achieving High-Strength Ductility Property in a Microstructure Homogenization Al-Zn-Mg-Cu Alloy by Electroshock Treatment

Study on the Aging Precipitation Behavior and Kinetics of Al-10.0Zn-3.0Mg-2.8Cu Alloy by Pre-Deformation Treatment

Gradient phase transformation of Al–Zn–Mg–Cu alloy induced by nonlinear interface wetting under electromagnetic shocking treatment

Evolution mechanism of grain orientation and texture distribution of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si alloy under electroshocking treatment

Reducing stress corrosion cracking susceptibility of high-strength aluminum alloy and its fastener by a novel electromagnetic shocking treatment

Hot Deformation Behavior and Microstructure Evolution of High-Strength Al-Zn-Mg-Cu Alloy

Experimental and Simulation Study for the Influence of Thermal Pre-Deformation on Subsequent Aging Precipitation Kinetics of Al-Zn-Mg-Cu Alloy

Optimizing strength and ductility in 7150 Al alloys via rapid electropulsing cyclic heat treatment

Influence mechanism of microstructure variation on mechanical properties of laser melting deposition Ti–6Al–4V alloy under electroshocking treatment

EFFECT OF PRE-DEFORMATION ON AGE- HARDENING AND MICROSTRUCTURE IN Al-Mg-Si-Cu ALLOY

The influence of precipitation on plastic deformation in a high Mg-containing AlMgZn-based crossover alloy: Slip localization and strain hardening

Microstructures and Mechanical Properties of Al-Zn-Mg-Cu Alloys under Multi-Directional Severe Strain and Aging

Effect of double-step homogenization treatments on the microstructure and mechanical properties of Al–Cu–Li–Zr alloy

Simultaneous enhancement of strength and ductility by combining heterogeneous microstructure and nanoprecipitates

Achieving excellent strength-ductility in Al–Si–Cu–Mg cast alloy via effective work hardening

Improved Ductility of Aged Mg-9Al-1Zn Alloy Strip by Electropulsing Treatment

Achieving high strength and high conductivity synergy through hierarchical precipitation stimulated structural heterogeneities in a Cu-Ag-Zr alloy

Achieving superior strength and ductility synergy in bulk ultrafine grained Al-Mg-Sc-Zr alloy via powder pre-aging

Study on the inhomogeneity of Al–Zn–Cu–Mg aluminum alloy plates with different thickness

Deformation mechanisms and mechanical properties of the high-strength and ductile Al-Zn-Mg-Cu alloys processed by repetitive continuous extrusion forming process with different heat treatments

An alternating ageing-annealing process for enhancing strength and ductility of a Mg-Gd-Y-Zn-Zr alloy