Abstract:Nanometer-sized particles, for example, TiO2, have gradually gained the attention to improve the mechanical and tribological properties of epoxy composite coatings. In the present paper, TiO2 with the size of 300 nm was applied to improve the reciprocating friction and wear performances of an epoxy composite. The effects of TiO2 content and sample preparation methods on the mechanical and tribological performances were investigated experimentally. It was found that the optimal mixture ratio of TiO2 was 4 wt%, and the tensile strength of composite increased by up to 30% compared with the control sample. The TiO2 nanoparticles were treated with polyvinylpyrrolidone (PVP) and then mixed into epoxy resin with three-roll mill grinding technique. The PVP molecules could surround a single TiO2 to form super-monomer, which produced repulsive force to aim to disperse nanoparticles, and the three-roll mill grinding could utilize the compression of axis surfaces and friction at different speeds to reduce the size of agglomerations of more than 5 microns. The results showed that the PVP molecules treatment could improve tensile strength and modulus, and three-roll mill grinding technique could enhance the elongation at break. In addition, the reciprocating wear rate and frictional coefficient of the epoxy composite plates also were reduced remarkably owing to the pretreatment of TiO2 particles, for example, and the frictional coefficient of epoxy composite decreased from 0.09 to 0.04 for the optimal ratio of TiO2, and special wear rate also decreased by 87.5% compared with the control sample. This was because the TiO2 nanoparticles acted as the stress transfer medium and could undertake part of loading to relieve stress directly into the epoxy matrix. There was a thin transfer film in which the particles acted as a membrane skeleton to avoid matrix further being torn. Because of the hardness and nanoeffect of particles, TiO2 could fill the defects in the wear interface to form a protective film and improve surface fatigue resistance property. The more uniform dispersion of TiO2 particles brought about the obvious improvement of wear resistance of composites.

Reinforced UHMWPE composites by grafting TiO2 on ATP nanofibers for improving thermal and tribological properties

Enhanced fretting wear performance of UHMWPE composites by grafting Co–Ni layered double hydroxides on attapulgite nanofibers

Carbon fiber modified by attapulgite for preparing ultra‐high molecular weight polyethylene composite with enhanced thermal, mechanical, and tribological properties

Attapulgite-graphene oxide hybrids as thermal and mechanical reinforcements for epoxy composites

Simultaneous Improvements in Wear Resistance and Mechanical Properties of Uhmwpe Nanocomposite Fabricated Via A Facile Approach

The tribological properties of PTFE filled with thermally treated nano-attapulgite

Tribological properties of kaolin filled UHMWPE composites in unlubricated sliding

Combined effects of interface modification and micro-filler reinforcements on the thermal and tribological performances of fabric composites

Effects of the Treatment of Attapulgite and Filler Contents on Tensile Properties of Ptfe and Attapulgite Reinforced Fabric Composites

Enhancement of Underwater Tribological Behavior of Hybrid Fabric Composites Using Ultrahigh Molecular Weight Polyethylene and Different Fillers

Enhanced thermal conductivity and wear resistance of polytetrafluoroethylene via incorporating hexagonal boron nitride and alumina particles

Significant friction and wear-reduction role of attapulgite nanofibers compounded in PEEK-Based materials

Reciprocating Friction and Wear Performances of Nanometer Sized‐tio2 Filled Epoxy Composites

Tribological and mechanical behaviors of Fe3O4NPs reinforced UHMWPE biocomposite

Preparation and Tribological Behaviors of Antigorite and Wollastonite Mineral Dual-Phase-Reinforced Polytetrafluoroethylene Matrix Composites

An Investigation on Tribological Properties and Mechanical Properties of UHMWPE/polycrystalline Mullite Fiber

Improved Tribological Properties of Poly(methyl methacrylate) Based Composites by the Synergistic Effect of Incorporating Ultra-High Molecular Weight Polyethylene and Heat Treatment

Attapulgite–MXene Hybrids with Ti3C2Tx Lamellae Surface Modified by Attapulgite as a Mechanical Reinforcement for Epoxy Composites

Tribological Properties of PTFE Filled with Modified Palygorskite and Wollastonite

Effects of modified attapulgite on the properties of attapulgite/epoxy nanocomposites

STUDY ON FRICTION AND WEAR PROPERTIES OF POTASSIUM TITANATE WHISKERS-REINFORCED PTFE COMPOSITES