Synergy of strong/weak interface adhesion forces and Li2S additive enabling high performance full anode-free lithium-metal batteries

Zejian Fang,Shukai Ding,Gaohui Du,Yong Zhu,Christophe Serra,Bingshe Xu,Qingmei Su,Guoquan Suo,Wei Wang

DOI: https://doi.org/10.1039/d3ta04883g

IF: 11.9

2023-11-08

Journal of Materials Chemistry A

Abstract:Anode-free Li-metal batteries (AFLBs) are receiving intense attention due to high theoretical capacity and the absence of Li metal. To attain AFLBs in practice, it is crucial to homogeneously plate Li on the Cu collector and develop an additional Li source. The controllable Li plating has been shown by an inorganic nanoparticle-based double-component solid electrolyte interface (SEI). However, the complicated and batch-to-batch non-reproducible fabrication process impedes its application. What's worse, the full AFLBs only depending on the homogeneous Li plating/stripping generally show poor performance due to less than 100% coulombic efficiency. Thus, the researcher still keeps a discreet attitude toward practical AFLBs. Herein, we present a polar crosslinked tripropylene glycol diacrylate nanoparticle (CTN) prepared by an organic molecule confinement reaction, which gives precise controllable physicochemical properties by a reproducible process. The double-component SEI on Cu collector is fabricated by blending CTN and PVDF at the weight ratio of 60/40, i.e., CTN-60. Attributing to a uniform Li+ transfer flux by the Li+ hopping between CTN in PVDF matrix and formation of interface voids by strong/weak adhesion force with Cu collector from the CTN and PVDF, respectively, the homogeneous Li plating is achieved by void-induced nucleation-growth mechanism. The result indicates a high coulombic efficiency of 96.08% after 200 cycles at a current density of 0.5 mA cm-2 and an areal capacity of 1 mAh cm-2 in half-cell AFLBs. In LiFePO4-based full ALIBs with CTN-60, the suspended Li2S electrolyte firstly is used for generation of Li at the first charge. The high performance is achieved at 171 mAh g-1 at 0.1 C, 84 mAh g-1 at 0.5 C, and 82 mAh g-1 at 2 C after 100 cycles.

materials science, multidisciplinary,chemistry, physical,energy & fuels