Abstract:A series of bifunctional catalysts based on beta zeolite were prepared though co-impregnation and tested for vapor-phase hydrodeoxygenation (VHDO) reaction to form phenol. Among the catalysts tested, 10Ni/Cu-Beta exhibited the highest stability, catalytic activity, and selectivity for phenol. Under the optimal conditions of a contact time (W/F) of 1.5 h, a molar flow of hydrogen to guaiacol (H/G) of 24, a time of stream (TOS) of 40min. A temperature of 450 degrees C, and a molar flow of stream to guaiacol (S/G) of 3, complete conversion was achieved, with a phenol yield of 63.95% and a sum yield of phenolic compounds of 96.89%. The beta zeolite support provided an adequate specific surface area and initial acid sites for the VHDO process. In the absence of water, the addition of Cu metal improved catalytic performance of the catalyst. However, the increase in temperature could result in more severe deactivation. The addition of water had little effect on the catalyst activity and helped to improve its stability to a certain extent. The loading of Ni metal contributed to an increased selectivity for phenol. The characterization results from X-ray diffraction (XRD) and hydrogen temperature-programed reduction (H2-TPR) showed that reduced and oxidized metals are finely dispersed on the catalyst surface. NH3 temperature-programed desorption and pyridine infrared resonance (Py-IR) characterizations revealed that the addition of Cu and Ni metal adjusts the type and amount of acid sites. A small part of Cu2+ and Ni2+ could be bound simultaneously to the surface of beta support, of which Cu2+ forms new metal-induced L-sites while Ni2+ does not, resulting in a lower concentration of L-sites on Ni/Cu-based catalysts compared to that on Cu-based catalysts and weakening the transmethylation reaction of phenolic compounds. The combination of metal sites and acid sites enabled the VHDO reaction of guaiacol to produce more phenol in the products.

Aqueous Phase Hydrodeoxygenation of Phenol on Hβ Zeolite Supported NiCo Alloy Catalysts

Upgrading Phenolic Compounds and Bio-Oil Through Hydrodeoxygenation Using Highly Dispersed Pt/TiO2 Catalyst

Conversion of Phenol to Cyclohexane in the Aqueous Phase over Ni/zeolite Bi-Functional Catalysts

Enhanced Phenol Hydrodeoxygenation over a Ni Catalyst Supported on a Mixed Mesoporous ZSM-5 Zeolite and Al2O3

Hydrogenation of Phenol to Cyclohexanol and Cyclohexanone on ZrO 2 -Supported Ni-Co Alloy in Water

Improved Hydrodeoxygenation of Phenol to Cyclohexane on NiFe Alloy Catalysts Derived from Phyllosilicates

Comparison of kinetics, activity and stability of Ni/HZSM-5 and Ni/Al 2 O 3 -HZSM-5 for phenol hydrodeoxygenation

Hydrodeoxygenation of Phenolics over Uniformly Dispersed Pt–Ni Alloys Supported by Self–Pillared Zsm–5 Nanosheets

Hydrodeoxygenation of Phenolic Compounds to Cycloalkanes over Supported Nickel Phosphides

Hydrogenation of Phenol to Cyclohexanone in Aqueous Phase on WO3 Modified Ni/ZrO2 Catalyst

Performance of a Ni-Cu-Co/Al2O3 Catalyst on In-Situ Hydrodeoxygenation of Bio-derived Phenol

Hydrodeoxygenation of Phenol as a Model Compound by Ni<sub>2</sub>P/HBeta-SBA-15

A highly dispersed Ni3P/HZSM-5 catalyst for hydrodeoxygenation of phenolic compounds to cycloalkanes

Aqueous Phase Hydrodeoxygenation of Phenol over Ni3P-CePO4 Catalysts

Hydrodeoxygenation of phenol as a model compound by Ni2P/HBeta-SBA-15,

A highly dispersed Ni<sub>3</sub>P/HZSM-5 catalyst for hydrodeoxygenation of phenolic compounds to cycloalkanes

Vapor-phase Hydrodeoxygenation of Guaiacol for Phenol Production Using Bifunctional Ni/Cu-Beta Zeolite Catalysts

Phyllosilicate-derived Ni/SiO2 Catalyst for Liquid-Phase Hydrodeoxygenation of Phenol: Synergy of Lewis Acid Sites and Ni0

Hydrogen source controlled hydrodeoxygenation of phenolic compounds to cycloalkanes/cycloalkanols over NiFeAlO x catalysts

The Hydrodeoxygenation of Phenol over Ni-P/Hβ and Ni-P/Ce-β: Modifying the Effects in Dispersity and Acidity

Phyllosilicate-derived Ni/SiO 2 catalyst for liquid-phase hydrodeoxygenation of phenol: Synergy of Lewis acid sites and Ni 0