Abstract:Tailorability is a key advantage of fiber-reinforced composites over other material systems. While tailoring a single isolated laminate is relatively simple, challenges arise when designing larger integrated components while ensuring compatibility between laminates and avoiding sharp changes in local stiffness. The innovative Double-Double (DD) laminate design method simplifies the optimization and processing of laminates by incorporating 4-ply building blocks consisting of +φ, −φ, +ψ, and −ψ ply orientations. As a relatively new concept, DD laminate design requires careful assessment to ensure that the performance of DD laminates is equivalent to that of conventional designs. The current study compares impact damage tolerance of quadriaxial (QUAD) laminates consisting of 0°, 90°, and ±45° ply orientations with equivalent DD laminates under Low-Velocity Impact (LVI) and Compression After Impact (CAI) loadings. To this end, a validated three-dimensional high-fidelity finite element model capable of capturing fiber breakage, splitting, kinking, as well as matrix cracking and delamination, was used. A computer tool was developed to identify equivalent DD laminates and to find the best stacking sequence for achieving layup homogenization. Three equivalent DD laminates were selected for the [0/45/90/−45] 4s . The first laminate had an equal in-plane stiffness [A] matrix ([67.5/–22.5/22.5/−67.5] 8T ), the second laminate had an equal flexural stiffness [D] matrix ([64.5/−17/17/−64.5] 8T ), and the third laminate ([65.5/−18.5/18.5/−65.5] 8T ) had a similar [D] matrix while keeping the difference between each element of [A] matrices below 10 %. The results indicate that the QUAD laminates can be replaced by equivalent DD without compromising impact damage tolerance while benefiting from the improved design and manufacturing ease of the DD laminate configuration.

Increase of shear fracture energy of adhesive joints using double-double laminates

Evaluation of the cracked lap shear test for mixed-mode fracture toughness estimation of adhesive joints

Damage onset in CFRP single lap joint for DD and QUAD laminates

Material and adhesive effect in adhesively-bonded composite stepped-lap joints

Low-velocity impact (LVI) and compression after impact (CAI) of Double-Double composite laminates

Assessment of Shear Fracture Energy in Hybrid Composites with Natural and Synthetic Fibers

Nonlinear Fracture Analysis of Delamination Crack Jumps in Laminated Composites

A study on the damage tolerance of durable redundant composite sandwich joints

Delamination Analysis of Carbon Fiber/Epoxy Composite Laminates under Different Loading Rates Using Acoustic Emission

EXPERIMENTAL INVESTIGATION ON ADHESIVE BONDED JOINTS OF CARBON FIBER COMPOSITE LAMINATES CONTAINING DISBOND DEFECT

Fracture Failure Prediction for Composite Adhesively Bonded Double Lap Joints by an Experiment-Based Approach

A Study of the Effects of Moisture on Composite-to-Metal Double-Lap Shear Joints

Developments in Laminate Modification of Adhesively Bonded Composite Joints

Empirical Characterization and Modeling of Cohesive – to – Adhesive Shear Fracture Mode Transition due to Increased Adhesive Layer Thicknesses of Fiber Reinforced Composite Single – Lap Joints

Delamination prevention of composite joints with asymmetric carbon-fiber reinforced plastic adherends

An Experimental and Numerical Study of Repairs on Composite Substrates with Composite and Aluminum Doublers Using Riveted, Bonded, and Hybrid Joints

Effect of hybridization and composite architecture symmetry in the bonded joint performance of jute/carbon fibre-reinforced composites

Experimental and numerical investigation on damage mechanism in asymmetric tapered laminates under tensile loading

Investigation of Residual Strength in CFRP Double-Adhesive Single Lap Bonded Joints after Low-velocity Impact

Modeling and analysis of Double-Double composite structures integrating piezoelectric materials

Experimental study of the influence of adhesive reinforcement in lap joints for composite structures subjected to mechanical loads