Abstract:Thin-ply composite failure modes also significantly differ from conventional ply composite failure modes, with the final failure mechanism switching from irregular progressive failure to direct fracture characterized by a uniform fracture with the reduction of the ply thickness. When open holes and bolt joints are involved, thin-ply-laminated composites exhibit more complex stress states, damage evolution, and failure modes. Compared to the experimental study of thin-ply-laminated composite-bolted joints, there are few reports about numerical analysis. In order to understand the damage evolution and failure mechanism of thin-ply-laminated composites jointed by single-lap bolt, a progressive damage model based on three-dimensional (3D) LaRC failure criterion combined with cohesive element is constructed. Through an energy-based damage evolution method, this model can capture some significant mechanical characteristics in thin-ply-laminated structures, such as the in situ effect, delamination inhibition, and fiber compressive kinking failure. The comparisons between the numerical predictions and experimental observations are made to verify the accuracy of the proposed model. It is found that the predicted stress-displacement curves, failure modes, damage morphologies, etc., are consistent with the experimental results, indicating that the presented progressive damage analysis method displays excellent accuracy. The predicted stress at the onset of delamination is 50% higher than that of the conventional thick materials, which is also consistent with experimental results. Moreover, the numerical model provides evidence that the microstructure of thin-ply-laminated composite performs better in uniformity, which is more conducive to inhibiting the intra-layer damage and the expansion of delamination damage between layers. This study on the damage inhibition mechanism of thin-ply provides a potential analytical tool for evaluating damage tolerance and bearing capabilities in thin-ply-laminated composite-bolted joints.

Damage onset in CFRP single lap joint for DD and QUAD laminates

Micro-damage Initiation Evaluation of Z-Pinned Laminates Based on a New Three-Dimension RVE Model

Effect of Z-pin Insertion Angles on Low-Velocity Impact Mechanical Response and Damage Mechanism of CFRP Laminates with Different Layups

Low-velocity impact (LVI) and compression after impact (CAI) of Double-Double composite laminates

A progressive damage model for carbon fiber-reinforced polymer laminates subjected to fastener pull-through failure

A 3D finite element model to simulate progressive damage in unidirectional- and woven-fibre thermoplastic discontinuous-long-fibre composites

Increase of shear fracture energy of adhesive joints using double-double laminates

Modeling Progressive Damage and Failure of Single-Lap Thin-Ply-Laminated Composite-Bolted Joint Using LaRC Failure Criterion

The Compressive Behavior of CFRP Laminates with Delamination of Different Shapes Using Numerical and Experimental Approaches

Progressive Damage Behavior of Composite L‐stiffened Structures with Initial Delamination Defects under Uniaxial Compression: Experimental and Numerical Investigations

Experimental investigation on open-hole CFRP laminate under combined loading using acoustic emission and digital image correlation

Experimental Investigation and Numerical Simulation of Bonded, Bolted, and Hybrid Joints in CFRP Laminates Under Tensile Loading

Finite Element Method of a Progressive Intralaminar and Interlaminar Damage Model for Woven Fibre Laminated Composites under Low Velocity Impact

Experiments and modelling of competitive failure behaviour of CFRP stepped-lap repairs with different design parameters

Experimental and numerical investigation of the damage propagation in regularly arrayed short fiber reinforced composite laminates under low‐velocity impact

The Role of Ply Angle in Interlaminar Delamination Properties of CFRP Laminates

Experimental and numerical study on the tensile failure behavior of toughened-interlayer composite laminates with automated fiber placement (AFP) induced gap and overlap defects

Post-buckling Progressive Damage of CFRP Laminates with a Large-Sized Elliptical Cutout Subjected to Shear Loading

Simulation and analysis of delamination damage propagation in CFRP structures

A novel damage characterization approach for laminated composites in the absence of material and structural information

A New Three-Dimensional Progressive Damage Model for Fiber-Reinforced Polymer Laminates and Its Applications to Large Open-Hole Panels