Abstract:Solid oxide fuel cell (SOFC) is a clean and efficient power generation device, which has been widely used in recent years. However, its operation lifetime still needs to be improved to meet the requirements for further commercialization. The performance degradation of SOFCs is affected by many factors. It is very important to distinguish these factors and determine the dominant factor(s) for improving the operation lifetime in a more efficient manner. In this paper, the initial operation stage (<100 h) of SOFCs is mainly focused, in which the electrochemical performance changes most significantly. The electrochemical impedance spectroscopy (EIS) was periodically monitored during the operation process. Individual electrode processes of button cells and industrial-size cells were distinguished via distribution of relaxation time (DRT) method and subsequent equivalent circuit model (ECM) fitting. Through detailed time-varying analysis of EIS, the changes of different electrode processes in the initial-stage operation were obtained, and the evolution mechanism of electrochemical performance was proposed. After reduction, SOFCs go through activation stage and aging stage in turn: i) In the activation stage, the anode porosity increases and the gas-phase diffusion process is enhanced, resulting in the improvement of cell performance. ii) In the aging stage, the Ni particles in the anode agglomerate, so the effective three phase boundary (TPB) density decreases, which leads to the degradation of anode charge transfer reaction and the drop of cell performance. This evolution mechanism of electrochemical performance was partially confirmed by detailed microstructure characterization. It should be mentioned that the duration of each stage and the performance change in each stage can be affected by the initial electrode structure. Therefore, in previous studies, it was observed that some cells did not show activation process during initial-stage operation, but directly entered the aging stage. Besides, during longer-term operation of the cell (>100 h), we speculate that the dominant degradation mechanism is the continuous increase of the anode interface reaction-related resistance, which is caused by the agglomeration of Ni particles. However, since the anode structure is gradually stable, the degradation rate of cell performance decreases with respect to the operation time.

Nickel Depletion and Agglomeration in SOFC Anodes During Long‐Term Operation

Microstructure degradation of Ni/CGO anodes for solid oxide fuel cells after long operation time using 3D reconstructions by FIB tomography

Ni / GDC Fuel Electrode for Low-Temperature SOFC and its Aging Behavior Under Accelerated Stress

Performance Evolution of Ni-YSZ Anode-Supported SOFCs During Initial-Stage Operation

Degradation of Ni-YSZ Electrodes in Solid Oxide Cells: Impact of Polarization and Initial Microstructure on the Ni Evolution

Long-term Stability of Metal-Supported Solid Oxide Fuel Cells Employing in Fi Ltrated Electrodes

Anode Degradation in SOFC: Fuel Impurity Effects on Nickel Component

Evolution of Electrochemical Characteristics of Solid Oxide Fuel Cells During Initial-Stage Operation

Fundamental mechanisms limiting solid oxide fuel cell durability

Role of Initial Microstructure on Nickel-Ysz Cathode Degradation in Solid Oxide Electrolysis Cells

Degradation Issues in Solid Oxide Electrolysers

Effects of operating conditions on the performance degradation and anode microstructure evolution of anode-supported solid oxide fuel cells

Quantifying the performance evolution of solid oxide fuel cells during initial aging process

Degradation analysis of commercial interconnect materials for solid oxide fuel cells in stacks operated up to 18000 hours

Electrochemical and Microstructural Characterization of Cyclic Redox Behaviour of SOFC Anodes

Navigating the future of solid oxide fuel cell: Comprehensive insights into fuel electrode related degradation mechanisms and mitigation strategies

Understanding Degradation Behavior of Direct-Ammonia Solid Oxide Fuel Cells Using Nanoscale Analyses

Comparative study on solid oxide fuel cell anode microstructure evolution after long-term operation

Ni migration of Ni-YSZ electrode in solid oxide electrolysis cell: An integrated model study

Impact of yttria-stabilized zirconia contents in nickel cermet anodes for intermediate temperature-operated syngas-fueled thin film solid oxide fuel cells

Long-Term Operation and Post Analysis of a Stack with Methane Fuel