Fabrication of Ultralow Ice-Adhesion Slippery Liquid Infused Porous Surfaces on Aluminum Alloy (7075-T651)

Yuan Yuan,Liang Wang,Guoyong Liu,Ruijin Liao
DOI: https://doi.org/10.3390/coatings10111025
IF: 3.236
2020-10-24
Coatings
Abstract:Slippery liquid infused porous surfaces (SLIPS) have been considered to be potential and effective method for anti-icing. Much work needed to be done for the application in field. In this study, SLIPS were successfully fabricated on 7075-T651 aluminum alloy by anodizing in phosphoric acid solution with three different voltage parameters and coating lubricant. Then the most suitable anodization parameters of samples were selected through the anti-icing performance tests. The best as-prepared surface exhibited ultralow ice-adhesion strength, which reduced from 261 to 6 kPa. Meanwhile, the freezing time of water-drop on aluminum alloy surfaces have been dramatically delayed at −5 and −10 °C (humidity of 75% ± 5%), respectively. Moreover, the durability of the SLIPS have also been investigated. Cycles of icing/deicing, mechanical damage, thermal and UV exposure were used to investigate the durability of SLIPS, and SLIPS could still show low ice-adhesion strength.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
The paper attempts to address the issue of icing on the surface of aluminum alloys, particularly the 7075-T651 aluminum alloy widely used in aircraft manufacturing. Specifically, the goal of the research is to develop Slippery Liquid-Infused Porous Surfaces (SLIPS) with ultra-low ice adhesion strength to enhance the anti-icing performance of the material and ensure the durability of these surfaces in practical applications. ### Main Issues: 1. **Insufficient anti-icing performance**: Existing anti-icing methods are ineffective for aluminum alloys, especially the 7075-T651 aluminum alloy. Aircraft icing can lead to flight accidents, thus new anti-icing technologies need to be developed. 2. **Limitations of superhydrophobic surfaces**: Although superhydrophobic surfaces (contact angle greater than 150°, contact angle hysteresis less than 10°) are considered potential anti-icing methods, they tend to fail in low-temperature and high-humidity environments and have poor durability. 3. **Durability of SLIPS**: Despite SLIPS showing good anti-icing performance under laboratory conditions, their durability (such as mechanical wear, thermal stability, UV exposure, etc.) needs further validation in practical applications. ### Solutions: - **Preparation of SLIPS**: By performing anodic oxidation treatment in phosphoric acid solution, a porous structure is created on the aluminum alloy surface, and a lubricant is applied to form SLIPS. - **Optimization of parameters**: Samples are prepared using different anodic oxidation voltage parameters (110V, 120V, 130V) to select the optimal parameters for anti-icing performance. - **Performance testing**: The anti-icing performance and durability of SLIPS are evaluated through ice adhesion strength tests, ice delay time tests, and durability tests (including mechanical wear, thermal stability, and UV exposure). ### Main Conclusions: - **Ultra-low ice adhesion strength**: The ice adhesion strength on the optimally prepared SLIPS surface is reduced from 261 kPa to 6 kPa, significantly improving the anti-icing performance. - **Ice delay time**: The freezing time of water droplets on the SLIPS surface is significantly extended, especially under conditions of −5°C and −10°C. - **Good durability**: SLIPS maintain low ice adhesion strength after multiple freeze/thaw cycles, mechanical wear, thermal stability, and UV exposure, demonstrating good durability. In conclusion, the study successfully developed a SLIPS surface suitable for 7075-T651 aluminum alloy, which not only significantly improves anti-icing performance but also ensures durability in practical applications.