Fabrication of Slippery Surfaces on Aluminum Alloy and Its Anti-Icing Performance in Glaze Ice

Bo Li,Jie Bai,Lei Fan,Xianyin Mao,Zhimin Ding,Hao Mu,Guoyong Liu,Yuan Yuan

DOI: https://doi.org/10.3390/coatings13040732

IF: 3.236

2023-04-04

Coatings

Abstract:Slippery liquid-infused porous surfaces (SLIPS) have received growing attention as promising icephobic materials. In this study, SLIPS were prepared on aluminum alloys by combining anodization and infusion of common silicone oil. An SLIPS with low ice-adhesion strength (6 kPa) was obtained by optimizing the anodizing time parameters (10 min). In addition, the frosting process and freezing of water droplets on the as-prepared SLIPS at −10 °C were delayed for 2000 s and 4800 s, respectively. Simultaneously, the as-prepared SLIPS also exhibited excellent anti-icing performance in glaze ice, since the supercooled water drips/ice slipped from the surface. The ice weight of the as-prepared SLIPS was significantly lower than that of the bare aluminum surface and the anti-icing-fluid-coated aluminum surface, which was reduced by 38.2%–63.6% compared with the bare aluminum surface. The ice weight increased with decreased temperature and inclination angle. This work proposes a method suitable for large-area preparation of SLIPS that achieves excellent anti-icing performance and significantly reduces the weight of glaze ice.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

The problem that this paper attempts to solve is the problem of equipment failure and potential safety hazards caused by icing of outdoor infrastructure (such as transmission lines, aircraft surfaces, etc.) in extremely cold weather. Specifically, the authors improve the anti - icing performance of aluminum alloy materials by preparing slippery liquid - infused porous surfaces (SLIPS), especially for glaze ice, a high - density and strongly adherent ice form. The paper mentions that traditional anti - icing methods have disadvantages such as high energy consumption, complex equipment, and being environmentally unfriendly, and passive anti - icing methods, such as constructing super - hydrophobic surfaces (SHSs), although they can reduce ice formation and adhesion under laboratory conditions, they are not effective in low - temperature and high - humidity environments. Therefore, this paper proposes a method combining anodization and silicone oil injection to prepare SLIPS on aluminum alloys to achieve low ice adhesion, delay the frosting and freezing processes, and significantly reduce the weight of glaze ice, thereby improving anti - icing performance.

The main contributions of the paper are as follows:
1. **Preparation method**: A fast, economical and effective method for preparing SLIPS on large - area aluminum alloy materials is proposed.
2. **Performance test**: The excellent anti - icing performance of the prepared SLIPS is verified through ice adhesion tests, anti - freezing tests and artificial glaze ice simulation experiments.
3. **Optimization parameters**: By changing the anodization time, the microstructure of SLIPS is optimized to obtain the best anti - icing effect, and the SLIPS prepared with an anodization time of 10 minutes shows the lowest ice adhesion (6 kPa).

In short, this research aims to develop an efficient and economical anti - icing technology to deal with the icing problem of outdoor infrastructure in extremely cold conditions.