Synthesis and Characterization of 2,5-Furandicarboxylic Acid Poly(butanediol Sebacate-Butanediol) Terephthalate (pbset) Segment Copolyesters with Excellent Water Vapor Barrier and Good Mechanical Properties
Feng Yu,Li Yingchun,Ye Xinming,Li Zhimao,Wang Wensheng,Liu Tong,Azab Islam H. El,Mersal Gaber A. M.,Ibrahim Mohamed M.,El-Bahy Zeinhom M.,Huang Mina,Guo Zhanhu
DOI: https://doi.org/10.1007/s10853-022-07269-7
IF: 4.5
2022-01-01
Journal of Materials Science
Abstract:In order to improve the performance of biodegradable materials, aliphatic–aromatic copolyesters were synthesized from sebacic acid, terephthalic acid, 1,4-butanediol and 2,5-furandicarboxylic acid via two-step esterification and polycondensation. Copolyesters were characterized by intrinsic viscosity, gel permeation chromatography, X-ray diffraction, Fourier infrared spectroscopy, nuclear magnetic resonance, differential scanning calorimetry, thermogravimetric analysis, lipase biodegradation, tensile and cup method testing. All the copolyesters had a weight-averaged molecular weight over 61,000 g/mol or intrinsic viscosity over 1.1 dL/g when the 2,5-furandicarboxylic acid content was in the range from 2 to 10% of terephthalic acid content. Particularly, the tensile strength, yield strength, elongation at break, molecular weight and water vapor barrier of copolyesters were improved to different extents. Obviously, the addition of 2,5-furandicarboxylic acid did not significantly affect the glass transition temperature and thermal stability of polyesters. When the addition amount of 2,5-furandicarboxylic acid was 10%, the water vapor barrier of copolyester reached the highest, which was increased by 89% compared with PBAT. On the whole, the copolyesters with the addition of 6% of 2,5-furandicarboxylic acid had the best comprehensive performance, which was conducive to promoting the application of biodegradable agricultural mulching and food packaging film.