Abstract:Fillers have been widely used in natural rubber (NR) products. They are introduced to serve as a strategy for modifying the final properties of NR vulcanizates. Silica and calcium carbonate (CaCO3) are among the fillers of choice when the color of the products is concerned. In this case, a special focus was to compare the vulcanizing efficiency of NR filled with two different filler types, namely nano-sized silica and micrometer-sized CaCO3. This study focused on the effects of the loading level (10–50 parts per hundred parts of rubber, phr) on the final properties and structural changes of NR composites. The results indicated that increased filler loading led to higher curing torques and stiffness of the rubber composites irrespective of the type of filler used. The better filler dispersion was achieved in composites filled with CaCO3 which is responsible for less polarity of CaCO3 compared to silica. Good filler distribution enhanced filler–matrix interactions, improving swelling resistance and total crosslink density, and delaying stress relaxation. The modulus and tensile strength of both composites also improved over the content of fillers. The CaCO3-filled composites reached their maximum tensile strength at 40 phr, exceeding, by roughly 88%, the strength of an unfilled sample. Conversely, the maximum tensile strength of silica-filled NR was at 20 phr and was only slightly higher than that of its unfilled counterpart. This discrepancy was ascribed to the stronger rubber–filler interactions in cases with CaCO3 filler. Effective rubber–filler interactions improved strain-induced crystallization, increasing crystallinity during stretching and reducing the strain at which crystallization begins. In contrast, large silica aggregates with poor dispersion reduced the overall crosslink density, and degraded the thermomechanical properties, tensile properties, and strain-induced crystallization ability of the NR. The results clearly indicate that CaCO3 should be favored over silica as a filler in the production of some rubber products where high performance was not the main characteristic.

Natural rubber nanocomposites using polystyrene-encapsulated nanosilica prepared by differential microemulsion polymerization

Natural Rubber Blended with Polystyrene Nanoparticles Prepared by Differential Microemulsion Polymerization

Study of Thermal and Mechanical Behaviors of Flame Retardant Polystyrene-Based Nanocomposites Prepared Via In-Situ Polymerization Method

Effect of silica particle size and coating by natural latex on properties of styrene‐butadiene rubber/carbon black/silica composites

Comparative Investigation of Nano-Sized Silica and Micrometer-Sized Calcium Carbonate on Structure and Properties of Natural Rubber Composites

Natural Rubber Composites Reinforced with Green Silica from Rice Husk: Effect of Filler Loading on Mechanical Properties

Influence of Modified Nanosilica on the Performance of NR/EPDM Blends: Cure Characteristics, Mechanical Properties and Swelling Resistance

Enhanced Mechanical Properties of Natural Rubber by Block Copolymer-Based Porous Carbon Fibers

Nanosilica reinforced EPDM silicone rubber blends: Experimental and theoretical evaluation of mechanical and solvent sorption properties

Enhancing properties of natural rubber nanocomposites with hybrid fillers and ionic liquid

Processing Rheological Behavior of Functionalized Silica/natural Rubber Composites

Synergistic effects of silane‐modified carbon black and nano‐silica hybrid fillers on the performance of natural rubber compounds

Natural Rubber Nanocomposites: A Review

Rheological and Dynamic Mechanical Behaviors of Short Nylon Fiber and Silica Filled Natural Rubber Compounds

Hybrid Silica-Based Fillers in Nanocomposites: Influence of Isotropic/Isotropic and Isotropic/Anisotropic Fillers on Mechanical Properties of Styrene-Butadiene (SBR)-Based Rubber

The effect of nanostructured silica synthesis temperature on the characteristics of silica filled natural rubber composite

Rejuvenating the structure and rheological properties of silica nanocomposites based on natural rubber

Effect of Different Silane Coupling Agents In-Situ Modified Sepiolite on the Structure and Properties of Natural Rubber Composites Prepared by Latex Compounding Method

Surface modification of silica nanoparticles by a polyoxyethylene sorbitan and silane coupling agent to prepare high-performance rubber composites

Effect of nano-silica surface-capped by bis[3-(triethoxysilyl)propyl] tetrasulfide on the cure behaviors, mechanical properties, swelling resistance and microstructure of styrene-butadiene rubber/acrylonitrile-butadiene rubber nanocomposites

Compatibilization of Cellulose Nanocrystal-Reinforced Natural Rubber Nanocomposite by Modified Natural Rubber