Highly Efficient Interface Modification between Poly(Propylene Carbonate)-Based Solid Electrolytes and a Lithium Anode by Facile Graphite Coating

Lu-ke Zhang,Mao-xiang Jing,Hua Yang,Quan-yao Liu,Fei Chen,Wei-yong Yuan,Ming-quan Liu,Yong-sheng Ji,Xiang-qian Shen

DOI: https://doi.org/10.1021/acssuschemeng.0c05153

2020-11-06

Abstract:Solid-state lithium metal batteries attract much attention for their high theoretical specific capacity and safety. However, the poor interfacial combination between the solid electrolyte (SE) and Li anode usually results in unavoidable growth of Li dendrites and interfacial side reactions. In this work, we propose a simple and effective strategy to modify the interface of the electrolyte/Li anode by scraping a graphite layer on the electrolyte surface facing the anode. The graphite-modified solid electrolyte (G-SE) has a high electrochemical potential window exceeding 4.6 V and high ion conductivity of 3.08 × 10^–4 S·cm^–2 at ambient temperature. This G-SE membrane is suitable for high-voltage solid-state lithium metal batteries, the assembled NCM622/G-SE/Li cell shows an initial capacity of 160 mAh/g at 0.5 C and a retention capacity of 100 mAh/g after 200 cycles. The good electrochemical performance is attributed to the graphite interfacial modification; the graphite coating and Li can spontaneously react to form a LiC₆ layer, which improves the SE/Li interfacial combination and suppresses the growth of lithium dendrites and interfacial side reactions.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c05153?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c05153</a>.EDS point analysis for the Li sheet after cycling (Figure S1); enlarged images of <a class="internalNav" href="#fig6">Figure </a><a class="internalNav" href="#fig6">6</a>a (Figure S2); battery case with test window (Figure S3); C 1s XPS spectrum of the Li sheet with graphite after cycling (Figure S4); lithium metal optical microscope image (Figure S5); digital photo of the lithium metal after 24 h of lithium/G-SE/lithium battery shelving (Figure S6); and the ion transport number calculation table (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c05153/suppl_file/sc0c05153_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology