Profiling hot isostatically pressed canister‐wasteform interaction for pu bearing zirconolite‐rich wasteforms

Pranesh Dayal,Rifat Farzana,Yingjie Zhang,Gregory R. Lumpkin,Rohan Holmes,Gerry Triani,Daniel J. Gregg,Greg Lumpkin

DOI: https://doi.org/10.1111/jace.18458

IF: 4.186

2022-04-02

Journal of the American Ceramic Society

Abstract:Zirconolite‐rich full ceramic wasteforms designed to immobilize Pu‐bearing wastes were produced via HIPing using stainless steel (SS) and nickel (Ni) HIP canisters. A detailed profiling of the elemental compositions of the major and minor phases over the canister‐wasteform interaction zone was performed using SEM‐EDS characterisation. Bulk sample analyses from regions near the centre of the HIP canister were also conducted for both samples using XRD and SEM‐EDS. The sample with the Ni HIP canister showed almost no interaction zone with only minor diffusion of Ni from the inner wall of the canister into the near‐surface region of the wasteform. The sample with the SS HIP canister showed ∼100‐120 μm of interaction zone dominated by high temperature Cr diffusion from canister material to the wasteform with the Cr predominantly incorporated into the durable zirconolite phase. We also examined, for the first time, changes to the HIP canister wall thickness caused by HIPing and demonstrated that no canister wall thinning occurred. Instead, in the areas examined the canister wall thickness was observed to increase (up to ∼20%) due to the compression occurring during the HIP cycle. Further, only sparce formation of (Cr, Mn)‐rich oxide particles were noted within the HIP canister inner wall area immediately adjacent to the ceramic material, with no evidence for reverse diffusion of ceramic material. Though the HIP canister‐wasteform interaction extends to ∼120 μm when using a SS HIP canister for the system investigated, this translates to <<1 vol% for an industrial scale HIPed wasteform. Importantly, the HIP canister‐wasteform interactions did not produce any obviously less durable phases in the wasteform or had any detrimental impact on the HIP canister properties.This article is protected by copyright. All rights reserved

materials science, ceramics