Thermal behavior and reaction to fire of European beech (Fagus sylvatica) treated with various salts and mineralization formulations
Tom Franke,Erik Larnøy,Thomas Volkmer
DOI: https://doi.org/10.1016/j.firesaf.2023.104088
IF: 3.78
2024-01-02
Fire Safety Journal
Abstract:Wood is used as a construction material since ancient times. However, its attribute as a flammable material capable of catching fire is one of the greatest concerns for its usage in various applications in construction. Building elements made of wood such as constructive elements, facades, ceilings, walls or floorings made of wood can increase the fire load of a building and contribute to spreading of a flame. According to the European standard EN 13501-1, materials are classified in various classes in respect to their reaction to fire. According to the requirements which are demanded in the EN 13501-1, the majority of solid wood and wood products is classified in class D [1]. One way to reduce these drawbacks and improve wood's burning class is to use fire retardants. An assumed goal for a successful fire retardant for wood is to achieve the burning class B, which is frequently required for higher, larger or public buildings in many national building codes [2]. There is a wide variety of different fire retardants for wood. They can be categorized according to their mode of action, their chemical composition, or their application method [[3], [4], [5], [6]]. A lot of fire retardants contain halogen, phosphorus or heavy metal and thus, are under discussion of being ecological concern or under suspicion for being harmful to humans and animals [3,[7], [8], [9], [10]]. There is a demand for the substitution of those chemicals by non-hazardous substances. Different alternative approaches were investigated during the last years for wood and wooden products like: silica-based formulations such as water glass and alkoxysilane treatments, various inorganic/mineral fillers or nanocomposites [[11], [12], [13], [14], [15], [16]]. Another promising approach is the mineralization of solid wood by means of a wood modification with slightly water-soluble minerals. Natural mineralization or fossilization, such as phosphatization, carbonization or silification describes the long process of substituting the wood structural compound with minerals [17]. Artificial mineralization by means of wood modification, on the other hand, describes the process of depositing minerals in the cell lumens and cell walls. Various authors describe artificial mineralization processes to incorporate calcium carbonate (CaCO 3 ) in wood which leads to improved fire retardancy [[18], [19], [20], [21]]. Guo et al. [22] demonstrated a successful treatment of wood with the phosphorous based mineral struvite to improve fire retardancy. Franke and Volkmer [23,24] treated oak and beech with an in-situ precipitation of the mineral calcium oxalate in a two-step impregnation process. It was shown that the mineralization treatment led to an improved fire retardancy. Calcium oxalate is the salt of the organic acid oxalic acid. It occurs according to its hydrate form as the mineral whewellite or weddellite. It is known to be formed by plants such as rhubarb against herbivores or in humans as kidney stones. Calcium oxalate is slightly water soluble (0.7 mg/l) and therefore might be suitable as a highly fixed fire retardant for solid wood. The focus of the study is to investigate the thermal behavior and the reaction to fire of calcium oxalate treated beech ( Fagus sylvatica ). Since in-situ precipitation of calcium oxalate is carried out in a 2-step process, two formulations are applied to precipitate calcium oxalate in the wood. Both formulations consist of two water soluble salts. Potassium oxalate is used as a precursor in both formulations. As a second salt calcium chloride, respectively calcium acetate is used as precursor. Special emphasizes of the investigations is set on the impact of the precursor alone, the byproducts produced in the reaction, as well as pure and fixed calcium oxalate achieved after carrying out a leaching protocol on the performance against fire. Furthermore, the impact of the retention on the reaction to fire was investigated.
materials science, multidisciplinary,engineering, civil