Abstract:This research has demonstrated that SiO 2 impregnation under high vacuum pressure of − 90 kPa can significantly reduce porosity by almost 10%, and improve the mechanical and viscoelastic properties of spruce wood under dry and saturated states. Characterization methods, such as impact test, DMA, SEM, EDS, porosity and SAXS tests were conducted on non-treated and − 90 kPa treated spruce wood samples under dry, saturated and submerged states to analyze the synergistic effect of high vacuum SiO 2 impregnation pressure on wood properties. The results showed that high vacuum impregnation pressure had a significant positive reinforcing effect on wood's properties. It increased the impact resistance of wood under dry and saturated conditions. Additionally, the high vacuum impregnation technique was able to overcome the water-induced softening effect and caused a significant increase in the storage modulus through uniform dispersion of the SiO 2 particles in the wood's vascular structure. Consequently, the impregnation reinforced the wood and ameliorated its capacity to absorb energy. High vacuum impregnation was also able to counteract the plasticizing effect of the water molecules and significantly increased the loss modulus by increasing the internal friction and cohesion of the wood components with the addition of the nanoparticles to the vascular system, which increased the wood's capacity to transform and dissipate energy. Quantitatively and qualitatively, impregnation under a vacuum pressure of − 90 kPa exhibited an effective obstruction of the vascular structure of spruce wood. In all conditions, high vacuum-impregnated samples showed significant enhancements over non-treated samples. This research demonstrated that high vacuum SiO 2 impregnation is an effective wood processing technique. Multiple materials and applications could benefit from this research wherein high strain-rate deformations are expected to occur or when simultaneous elastic behaviour of wood and its damping energy is needed. This study could also pave the way for research on the synergistic effect of SiO 2 impregnation and water absorption on the viscoelastic behaviour of wood.

Effects of SiO2 Sol on Leachability of Wood Impregnated with Disodium Octaborate Tetrahydrate

Research on Fire Retardant Performance of Wood with the Compound of Potassium Carbonate and SiO2 Gels

Research On Fire Retardant Performance Of Chinese Fir With The Compound Of Disodium Octaborate Tetrahydrate And Sio2 Gels

Role of surface treatment on water absorption of poly(vinyl chloride) composites reinforced by Phyllostachys pubescens particles

Effect of Sepiolite-Loaded Fe<sub>2</sub>O<sub>3</sub> on Flame Retardancy of Waterborne Polyurethane

The study of physico-mechanical properties of SiO2-impregnated wood under dry and saturated conditions

Decay resistance and mechanical strength of poplar wood treated after injection treatment to living trees using ammoniacal copper quaternary/carbon dots

Flame-retardancy and Smoke Suppression Characteristics of Bamboo Impregnated with Silicate-Intercalated Calcium Aluminum Hydrotalcates

Adsorption Dynamics of Disodium Octaborate Tetrahydrate on Clay Minerals: Implications for Construction Wood Protection

Surface Treatment of Mongolian Scots Pine Using Phosphate Precipitation for Better Performance of Compressive Strength and Fire Resistance

In Situ Fabrication of a Superhydrophobic ORMOSIL Coating on Wood by an Ammonia–HMDS Vapor Treatment

Improvement of Mechanical, Hydrophobicity and Thermal Properties of Chinese Fir Wood by Impregnation of Nano Silica Sol

Organic–inorganic hybrid of silica sol to promote flame retardant and mechanical properties of wood

Building bridging structures and crystallization reinforcement in sodium silicate-modified poplar by dimethylol dihydroxyethylene urea

Flame Retardant Properties and Thermal Decomposition Kinetics of Wood Treated with Boric Acid Modified Silica Sol

Hydrophobic Modification of Bi2O3-Doped Si-Ti Composite Film on a Wood Surface

Preparation of multifunctional flame-retardant and superhydrophobic composite wood by iron ions doped phytic acid-based nanosheets

Enhancing wood stability and fire retardancy through citric acid and phosphorylated sucrose stearate cross-linking modification

Synergistic Effect of SiO2 on Intumescent Flame-retardant Polypropylene

Effect of Si-Al Compounds on Fire Properties of Ultra-Low Density Fiberboard

Preparations, characterizations, thermal and flame retardant properties of cotton fabrics finished by boron-silica sol-gel coatings