Abstract:This study investigates the structure–property relationship in a dissimilar joint between super duplex stainless steel (sDSS 2507) and pipeline steel (X-70) using gas tungsten arc welding and ER2594 filler. Tubing and risers used to transport hydrocarbons are regularly joined using these dissimilar metals. The microstructures of lower heat input (LHI-0.7 kJ/mm) and higher heat input (HHI-1.4 kJ/mm) weldments were examined to understand the influence of heat input on the structure–property relationship. The weldments' mechanical characteristics were tested via hardness, impact, and tensile tests. Base metal and weld zone/interface characterization were studied utilizing optical and scanning electron microscopes with energy-dispersive spectroscopy (EDS). Elemental variation was confirmed by EDS spectra, elemental line mapping, and electron probe microanalysis with wavelength-dispersive spectrometer along the weld interface and weld zone. Significant microstructure variation was observed in X-70 BM at the LHI and HHI weld interfaces. Type II boundary and macro-segregation forms like peninsulas and islands were present in both weldments. In LHI and HHI weldment, duplex microstructure dominates the weld zone cap and filler pass. In the backing pass, duplex microstructure replaces skeletal ferrite, which predominates in the root pass of the HHI weld zone. LHI weldment has an average microhardness of 275 ± 7 HV 0.5 , while HHI had 285 ± 5 HV 0.5 . Both weldment's tensile tests revealed that the sample fractured on the weaker X70 BM side. LHI and HHI weldments had 600 MPa and 610 MPa ultimate tensile strengths and 22% and 18% elongation percentages, respectively. LHI weldments (200 ± 7 J, 210 ± 4 J) and HHI weldments (210 ± 5 J, 220 ± 8 J) have lower average impact toughness in cap and root pass than the sDSS 2507 BM (320 ± 3 J) and X-70 BM (300 ± 6 J), respectively. The increase in heat input led to a minimal 2% difference in tensile strength, a notable 10% increase in hardness, and a slight 5% variation in impact toughness between LHI and HHI weldments. Marine and offshore applications may benefit from investigating the sDSS 2507/X-70 DWJ's process parameter selection, thermodynamic analysis, and structure–property relationship.

Assessing the Consequences of Repetitive Repair Welding in Shielded Metal Arc Welding (SMAW) on Material Properties in API 5L Grade B PSL 2 Welded Pipelines

PENGARUH REPAIR LAS GMAW TERHADAP KEKUATAN TARIK, KEKERASAN, DAN STRUKTUR MIKRO PADA MATERIAL BAJA A36

Effect of Repeated Weld Repairs on Microstructure and Mechanical Properties of Heat-Affected Zone in CA6NM Stainless Steel

Characterization of Mechanical Properties and Residual Stress in API 5L X80 Steel Welded Joints

Influence of filler metal on residual stress in multi-pass repair welding of thick P91 steel pipe

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Changes in microstructure and properties of weld heat-affected zone of high-strength low-alloy steel

Full-scale experimental investigation of the fracture behaviours of welding joints of APL X80 wide plate based on DIC technology

Post-Weld Heat Treatment of API 5L X70 High Strength Low Alloy Steel Welds

Impact of crack propagation path and inclusion elements on fracture toughness and micro-surface characteristics of welded pipes in DWTT

A Comparative Study on the Mechanical Behavior of S355J2 Steel Repair-Welded Joints

The effect of SMAW welding parameters on stress corrosion cracking of the X65 gas pipelines steel

Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment

Effect Of Mig Welding Process Parameters On Erosion And Corrosion Behavior Of Astm A106 Grade-B Pipe Weldments

Numerical and Experimental Analysis of Dissimilar Repair Welding Residual Stress in P91 Steel Considering Solid-State Phase Transformation

Prediction of static failure in metal inert gas welded nuclear grade pipe 347 SS: Experimentation and finite-element analysis approach

Structure–property relationship assessment of dissimilar gas tungsten arc welded joint of pipeline steel and super duplex stainless steel for marine applications

Failure analysis of L415/316L composite pipe welded joint

Effect of the welding technique on mechanical properties and metallurgical characteristics of the naval grade high strength low alloy steel joints produced by SMAW and GMAW

Effect of Microstructure on Mechanical Properties of X65MS Welded Pipe Joint